Influência do bismuto nas propriedades mecânicas do aço AISI M2 sinterizado
![Thumbnail](/bitstream/handle/10183/94792/000730985.pdf.jpg?sequence=3&isAllowed=y)
View/ Open
Date
2009Author
Type
Title alternative
Influence of the bismuth on mechanical properties of high speed steel AISI M2 sintered
Subject
Abstract in Portuguese (Brasil)
A adição de bismuto em uma liga de aço AISI M2 produzida por metalurgia do pó foi avaliada, buscando melhorar a usinabilidade e as propriedades mecânicas deste material. Para este estudo, foram analisadas as amostras de aço rápido AISI M2 com os seguintes teores de bismuto: 0.1%, 0.3%, 0.5% e 1%. O processo de conformação do pó realizou-se através da compactação uniaxial a 600 MPa e sinterização sob atmosfera protetora de 95%N2 + 5%H2. A temperatura de sinterização utilizada foi de 1.130°C. As ...
A adição de bismuto em uma liga de aço AISI M2 produzida por metalurgia do pó foi avaliada, buscando melhorar a usinabilidade e as propriedades mecânicas deste material. Para este estudo, foram analisadas as amostras de aço rápido AISI M2 com os seguintes teores de bismuto: 0.1%, 0.3%, 0.5% e 1%. O processo de conformação do pó realizou-se através da compactação uniaxial a 600 MPa e sinterização sob atmosfera protetora de 95%N2 + 5%H2. A temperatura de sinterização utilizada foi de 1.130°C. As amostras apresentaram um aumento proporcional da porosidade com o acréscimo percentual de bismuto. No ensaio de desgaste e de compressão a amostra de 0,3% de bismuto apresentou menor resistência mecânica. No ensaio de usinabilidade as amostras de M2 e a M2 com 1% de bismuto sinterizado obtiveram cavacos cisalhados (forma de agulha) e cavaco lamelados (na forma arcos), respectivamente. ...
Abstract
The addition of bismuth in an alloy steel AISI M2 produced by powder metallurgy, has been evaluated aiming to improve the machinability and mechanical properties of this material. For this study, were analyzed samples of AISI M2 steel quick with the following levels of bismuth: 0.1%, 0.3%, 0.5% and 1%. The process of shaping the powder was carried out by uniaxial compaction at 600 MPa and sintering in protective atmosphere of 95% N2 + 5% H2. The sintering temperature used was 1130 ° C. The samp ...
The addition of bismuth in an alloy steel AISI M2 produced by powder metallurgy, has been evaluated aiming to improve the machinability and mechanical properties of this material. For this study, were analyzed samples of AISI M2 steel quick with the following levels of bismuth: 0.1%, 0.3%, 0.5% and 1%. The process of shaping the powder was carried out by uniaxial compaction at 600 MPa and sintering in protective atmosphere of 95% N2 + 5% H2. The sintering temperature used was 1130 ° C. The samples showed a proportional increase of porosity with increasing percentage of bismuth. In the test of wear and compression of the sample of 0.3% of bismuth showed lower mechanical strength. Machinability testing of the samples of M2 and M2with 1% of bismuth sintered obtained chips shear (in the form of needle) and chip block (as arcs), respectively. ...
In
Estudos tecnológicos em Engenharia. São Leopoldo, RS. Vol. 5, n. 3 (set. /dez. 2009), p. 421-430