dc.contributor.authorAso, Adriana Miwapt_BR
dc.contributor.authorKnewitz, Fábio Luispt_BR
dc.contributor.authorMartins, Viniciuspt_BR
dc.contributor.authorRodrigues, Wilson Correapt_BR
dc.contributor.authorRocha, Alexandre da Silvapt_BR
dc.contributor.authorSchaeffer, Liriopt_BR
dc.date.accessioned2014-04-26T01:53:13Zpt_BR
dc.date.issued2009pt_BR
dc.identifier.issn1808-7310pt_BR
dc.identifier.urihttp://hdl.handle.net/10183/94792pt_BR
dc.description.abstractA adição de bismuto em uma liga de aço AISI M2 produzida por metalurgia do pó foi avaliada, buscando melhorar a usinabilidade e as propriedades mecânicas deste material. Para este estudo, foram analisadas as amostras de aço rápido AISI M2 com os seguintes teores de bismuto: 0.1%, 0.3%, 0.5% e 1%. O processo de conformação do pó realizou-se através da compactação uniaxial a 600 MPa e sinterização sob atmosfera protetora de 95%N2 + 5%H2. A temperatura de sinterização utilizada foi de 1.130°C. As amostras apresentaram um aumento proporcional da porosidade com o acréscimo percentual de bismuto. No ensaio de desgaste e de compressão a amostra de 0,3% de bismuto apresentou menor resistência mecânica. No ensaio de usinabilidade as amostras de M2 e a M2 com 1% de bismuto sinterizado obtiveram cavacos cisalhados (forma de agulha) e cavaco lamelados (na forma arcos), respectivamente.pt_BR
dc.description.abstractThe addition of bismuth in an alloy steel AISI M2 produced by powder metallurgy, has been evaluated aiming to improve the machinability and mechanical properties of this material. For this study, were analyzed samples of AISI M2 steel quick with the following levels of bismuth: 0.1%, 0.3%, 0.5% and 1%. The process of shaping the powder was carried out by uniaxial compaction at 600 MPa and sintering in protective atmosphere of 95% N2 + 5% H2. The sintering temperature used was 1130 ° C. The samples showed a proportional increase of porosity with increasing percentage of bismuth. In the test of wear and compression of the sample of 0.3% of bismuth showed lower mechanical strength. Machinability testing of the samples of M2 and M2with 1% of bismuth sintered obtained chips shear (in the form of needle) and chip block (as arcs), respectively.en
dc.format.mimetypeapplication/pdfpt_BR
dc.language.isoporpt_BR
dc.relation.ispartofEstudos tecnológicos em Engenharia. São Leopoldo, RS. Vol. 5, n. 3 (set. /dez. 2009), p. 421-430pt_BR
dc.rightsOpen Accessen
dc.subjectHigh speed steelen
dc.subjectMetalurgia do pópt_BR
dc.subjectAço rápidopt_BR
dc.subjectBismuthen
dc.subjectPowder metallurgyen
dc.subjectMachiningen
dc.titleInfluência do bismuto nas propriedades mecânicas do aço AISI M2 sinterizadopt_BR
dc.title.alternativeInfluence of the bismuth on mechanical properties of high speed steel AISI M2 sintered en
dc.typeArtigo de periódicopt_BR
dc.identifier.nrb000730985pt_BR
dc.type.originNacionalpt_BR