Influence of milling time during the mechanical alloying process on the properties of Fe-3Si-0.75P alloy
View/ Open
Date
2015Author
Type
Subject
Abstract
In this study the soft magnetic alloy Fe-3Si-0.75P (wt%) was obtained by mechanical alloying through powder metallurgy. The processing included the formulation of metallic powder, wet milling for 1 h, 3 h, 6h and 9 h, in an attritor mill using alcohol P.A. as a lubricant. Cold compaction was then performed in a floating die under 600 MPa pressure and, finally the ring-shaped test specimens were sintered at 1150 °C for 1h. The electrical, physical and magnetic properties were then analyzed using ...
In this study the soft magnetic alloy Fe-3Si-0.75P (wt%) was obtained by mechanical alloying through powder metallurgy. The processing included the formulation of metallic powder, wet milling for 1 h, 3 h, 6h and 9 h, in an attritor mill using alcohol P.A. as a lubricant. Cold compaction was then performed in a floating die under 600 MPa pressure and, finally the ring-shaped test specimens were sintered at 1150 °C for 1h. The electrical, physical and magnetic properties were then analyzed using the following assays: Laser granulometry, density, metallography, hysteresis curve and AC permeability, resistivity and XRD. The results showed a strong influence of milling time on magnetic properties of the alloy. There was a decrease in grain size with the milling time, which is likely the cause of increased in magnetic properties. ...
In
Materials research : ibero-american journal of materials. São Carlos, SP. Vol. 18, n. 5 (Sept./Oct. 2015), p. 1070-1076
Source
National
Collections
-
Journal Articles (39559)Engineering (2413)
This item is licensed under a Creative Commons License