Methodology for determination of degree of nodulalaarity in a ductile castiron GGG 40 by ultrasonic velocity test
Fecha
2018Autor
Materia
Abstract
Cast iron alloys combine many elements such as carbon, iron, silicon, magnesium and can be usually classified according to their microstructure in ductile, gray, compacted, white, and malleable. Each one has particularities in terms of properties and applications. Hence, this study aims to evaluate the degree of nodularity (%) in a ductile cast iron alloy GGG 40. In this context, a methodology to investigate the degree of nodularity was proposed. The ultrasonic method was used to determine the ...
Cast iron alloys combine many elements such as carbon, iron, silicon, magnesium and can be usually classified according to their microstructure in ductile, gray, compacted, white, and malleable. Each one has particularities in terms of properties and applications. Hence, this study aims to evaluate the degree of nodularity (%) in a ductile cast iron alloy GGG 40. In this context, a methodology to investigate the degree of nodularity was proposed. The ultrasonic method was used to determine the amount of ductile graphite as well as for parts release and thus facilitated the industrial operational execution. The effect of ultrasonic sound was investigated in sixtyseven ductile cast irons, and these analyses were further compared to the level of nodularity observed by metallography. Finally, based on the findings, the cast iron quality was guaranteed, leading to time-savings, avoiding the microstructural examination, and thus promoting cost reductions. ...
En
Southern Brazilian Journal of Chemistry. Porto Alegre. Vol. 26, no. 26 (Dec. 2018), p. 10-16
Origen
Nacional
Colecciones
-
Artículos de Periódicos (39552)Ingeniería (2413)
Este ítem está licenciado en la Creative Commons License