dc.description.abstractNeste estudo foram desenvolvidos compósitos utilizando PEAD, pó de madeira (Pinus taeda), alumina calcinada e dois diferentes tipos de agentes compatibilizantes para avaliação das propriedades morfológicas e mecânicas dos mesmos. Para aumentar a interação entre a matriz polimérica e o pó de madeira foram utilizados 2% de polietileno graftizado com anidrido maleico em todas as formulações. Para efeito comparativo foi desenvolvida uma formulação com viniltrietoxisilano como compatibilizante para a alumina calcinada. O teor de cargas variou de 4% a 33% para os compósitos de carga única e mantiveram o percentual de 28% para os compósitos com as duas cargas. A interação entre a matriz polimérica e as cargas, proporcionada pelo agente compatibilizante anidrido maleico, foi observada nas micrografias da interface da matriz/carga. A utilização do silano não proporcionou efeito adicional nas propriedades mecânicas dos compósitos. Os compósitos isentos de alumina apresentaram maior resistência à tração, porém na resistência à flexão a presença da alumina contribuiu para o aumento desta propriedade provavelmente devido à pequena interação existente entre a interface do seu grão e a matriz polimérica.pt_BR
dc.description.abstractThis work aims at the evaluation of morphological and mechanical properties of HDPE composites developed with wood flour (Pinus taeda), calcined alumina and two different types of compatibilizing agents. In order to improve the interaction between the polymer matrix and wood flour 2% maleic anhydride-grafted polyethylene was used in all formulations. For comparison a formulation with triethoxyvinylsilane as compatibilizer for the calcined alumina was developed. The filler content ranged from 4% to 33% for the single filler composite while the percentage of 28% was kept as such for the two-fillers composites. The interaction between the polymer matrix and fillers, provided by the maleic anhydride compatibilizer agent, could be observed in the micrographs of the matrix / filler interface. The silane did not improve the mechanical properties of the composite. Free alumina composites showed higher tensile strength, but concerning flexural strength the presence of alumina contributed to increased values in this property. This was probably caused by the reduced interaction between the interface of its grain and the polymer matrix.en
dc.format.mimetypeapplication/pdf
dc.language.isoporpt_BR
dc.relation.ispartofPolímeros (São Carlos): ciência e tecnologia. São Carlos, SP. Vol. 25, no. 4 (July/Aug. 2015), p. 408-413pt_BR
dc.rightsOpen Accessen
dc.subjectCompositeen
dc.subjectCompósitospt_BR
dc.subjectHDPEen
dc.subjectPolietileno de alta densidadept_BR
dc.subjectwood flouren
dc.subjectAluminapt_BR
dc.subjectCalcined aluminaen
dc.subjectAnidrido maleicopt_BR
dc.subjectPropriedades mecânicaspt_BR
dc.subjectMaleic anhydrideen
dc.titleAvaliação das propriedades mecânicas e morfológicas de compósitos de PEAD com pó de Pinus taeda e alumina calcinadapt_BR
dc.title.alternativeAvaliação das propriedades mecânicas e morfológicas de compósitos de polietileno de alta densidade com pó de Pinus taeda e alumina calcinada pt_BR
dc.title.alternativeEvaluation of the mechanical and morphological properties of HDPE composites with powdered Pinus taeda and calcined alumina en