dc.description.abstractRevestimentos orgânicos anticorrosão normalmente possuem cargas lamelares que aumentam o caminho de difusão do O2 e H2O até a interface polímero/metal atuando, portanto, como barreira. Em caso de avaria mecânica do revestimento e surgimento de micro-trincas, um novo método de reparação self-healing foi obtido pelo uso de revestimentos inteligentes (smart coatings). Estes revestimentos possuem inibidores de corrosão incorporados em sua matriz que promovem lenta e localizada liberação do agente inibidor. Neste trabalho se processou carepa de aço carbono laminado para utilização como carga em resina alquídica, com a finalidade de melhorar a propriedade de barreira. As carepas de aço AISI 316 e 420 também foram estudadas. Estas foram investigadas como possíveis fornecedoras de cromatos (AISI 420) e/ou molibdatos (AISI 316) por lenta liberação e solubilização destes inibidores anódicos. As carepas foram inicialmente lavadas, moídas e ustuladas. Depois caracterizadas química e morfologicamente por MEV-EDS, a distribuição de tamanhos de partículas foi determinada por espalhamento de luz, as fases foram quantificadas por análise de Raios-X e Rietveld e para as medições de taxa de cátions metálicos dissolvidos durante lixiviação, foi usado espectrometria de absorção atômica. A taxa de liberação de ions cromatos e molibdatos foram descriminadas por carepas ustuladas e não ustuladas. As lixívias foram realizadas em água deionizada e solução de ácido fosfórico com pH 4,5, simulando o pH que ocorre durante a corrosão do Fe. Os revestimentos desenvolvidos foram aplicados sobre placas de aço SAE 1006LF. Os métodos usados para a avaliação do desempenho destes revestimentos foram névoa salina e imersão das amostras em solução de NaCl 0,1M para medições periódicas de impedância (EIS). Os resultados indicam que a carepa de aço AISI 1020 aumenta a propriedade de barreira do filme polimérico, bem como uma redução da progressão na capacitância dos revestimentos que continham carepa de aço AISI 420, devido à permeação de H2O. Revestimentos contendo carepas de aços AISI 420 ou AISI 316 apresentaram maior resistência em amostras riscadas, revelando um efeito benéfico dos espinélios Cr e Mo, representando um possível efeito smart coating.pt_BR
dc.description.abstractOrganic coatings for corrosion protection usually have additions of lamellar inorganic charges that should increase the diffusion path of O2 and H2O to the metal/polymer interface. In the case of mechanical damage of the coating by the occurrence of micro-cracks, a new method of self-healing has been developed, which involve the local release of inhibitors only in the case of corrosion attack of the metallic substrate, characterizing the so called smart coatings. In this work, hot-rolled carbon steel scales were processed for the use as lamellar charge in alkyd resins to improve the barrier property of the obtained coating. Additionally scales of the stainless steels AISI 316 and 420 were studied, but in this case, as possible sources of chromate (AISI 420) and/or molybdate (AISI 316) by slow solubilization and release of these anodic inhibitors. Scales were initially washed, milled and calcined. Later, the morphology was characterized by SEM-EDS, the size distribution of particles determined by light scattering, the phases quantified by XRD and Rietveld analysis [1], while for the measurement of release rates of dissolved metal cations, atomic absorption spectrometry was used. Long chained alkyd resin was used for the production of five different paints, four of these with the addition of 4.5 weight % of Fe-oxides, and for comparison, one free of additional inorganic charges. The release rate of chromate and molybdate ions was determined for calcined and non calcined scales. The aqueous extraction was carried out in deionized water and pH 4.5 phosphate solution, simulating the pH on a corroding Fe surface. The developed coatings were applied on SAE 1006LF steel plates and the corrosion resistance evaluated in salt spray and by periodic EIS measurements of samples immersed in NaCl 0,1M. The results indicate that the addition of “AISI 1020” scale increases the barrier property of the polymeric film, and the addition of “AISI 420” scale slow down the capacitance evolution due to water permeation. Coatings containing "AISI 420 or AISI 316 scales additions have clearly a higher corrosion resistance of scratched coupons, showing the beneficial action of the (Cr, Mo)-spinels additions and a possible smart coating effect.en
dc.format.mimetypeapplication/pdfpt_BR
dc.language.isoporpt_BR
dc.rightsOpen Accessen
dc.subjectInibidores de corrosãopt_BR
dc.subjectAço-carbonopt_BR
dc.subjectRevestimentopt_BR
dc.titleDesenvolvimento de revestimentos contendo adições de carepas de laminação de açospt_BR
dc.typeDissertaçãopt_BR
dc.identifier.nrb000915193pt_BR
dc.degree.grantorUniversidade Federal do Rio Grande do Sulpt_BR
dc.degree.departmentEscola de Engenhariapt_BR
dc.degree.programPrograma de Pós-Graduação em Engenharia de Minas, Metalúrgica e de Materiaispt_BR
dc.degree.localPorto Alegre, BR-RSpt_BR
dc.degree.date2012pt_BR
dc.degree.levelmestradopt_BR


Thumbnail
   

Este item está licenciado na Creative Commons License

Mostrar registro simples