Avaliação da resistência de união à dentina dos cimentos à base de MTA e à base de resina epóxica, através do teste de micro push-out
Fecha
2010Autor
Tutor
Nivel académico
Especialización
Materia
Resumo
Objetivo: Avaliar a resistência de união à dentina de três cimentos endodônticos, dois à base de MTA, Endo-C.P.M.-Sealer® e Fillapex, e um à base de resina epóxica, AH Plus®, através do teste de micro push-out. Materiais e métodos: Um total de 45 dentes humanos monorradiculares extraídos foram preparados através da técnica escalonada. Realizou-se irrigação com NaOCl 2,5% a cada troca de instrumento e irrigação final com EDTA 17% e água destilada. Os canais foram obturados da seguinte maneira: g ...
Objetivo: Avaliar a resistência de união à dentina de três cimentos endodônticos, dois à base de MTA, Endo-C.P.M.-Sealer® e Fillapex, e um à base de resina epóxica, AH Plus®, através do teste de micro push-out. Materiais e métodos: Um total de 45 dentes humanos monorradiculares extraídos foram preparados através da técnica escalonada. Realizou-se irrigação com NaOCl 2,5% a cada troca de instrumento e irrigação final com EDTA 17% e água destilada. Os canais foram obturados da seguinte maneira: grupo I, Endo-C.P.M.-Sealer e guta-percha; grupo II, Fillapex e guta-percha; e grupo III, AH Plus e guta-percha. Os dentes foram cortados em fatias transversais após sete dias. Cada fatia foi submetida ao teste de micro push-out. Os dados obtidos foram analisados através do teste de Kruskal-Wallis e PostHoc de Dunn com nível de significância de 5%. Resultados: O cimento Endo-C.P.M.-Sealer apresentou os valores mais altos de resistência de união à dentina (8,265 MPa). Já os espécimes obturados com Fillapex (2,041 MPa) e AH Plus (3,034 MPa) não apresentaram diferença estatisticamente significativa entre eles. Conclusões: A força de resistência de união à dentina através do teste de micro push-out foi maior nos espécimes obturados com o cimento à base de MTA, Endo- C.P.M.-Sealer. ...
Abstract
Aim: To evaluate the bond strength to root dentin of three root canal sealers, two of them MTA-based, Endo-C.P.M.-Sealer® and Fillapex, and one epoxy resin-based, AH Plus®, using the micro push-out test. Methods: A total of 45 extracted human teeth with single canal were prepared by the scale technique. Irrigation was performed with 2.5% NaOCl between each instrument and a final rinse with 17% EDTA and distilled water. Canals were filled as follows: group I, Endo-C.P.M.-Sealer and gutta-percha; ...
Aim: To evaluate the bond strength to root dentin of three root canal sealers, two of them MTA-based, Endo-C.P.M.-Sealer® and Fillapex, and one epoxy resin-based, AH Plus®, using the micro push-out test. Methods: A total of 45 extracted human teeth with single canal were prepared by the scale technique. Irrigation was performed with 2.5% NaOCl between each instrument and a final rinse with 17% EDTA and distilled water. Canals were filled as follows: group I, Endo-C.P.M.-Sealer and gutta-percha; group II, Fillapex and gutta-percha; and group III, AH Plus and gutta-percha. After seven days, the samples were cut into sections. The slices obtained were subjected to the micro push-out test. The data were analyzed using the Kruskal-Wallis and Dunn PostHoc test at a significance level of 5%. Results: Endo-C.P.M.-Sealer showed the highest values of bond strength to root dentin (8.265 MPa). The specimens filled with Fillapex (2.041 MPa) and AH Plus (3.034 MPa) showed lower levels and no statistically significant difference between each other. Conclusions: The Bond strength through the micro push-out test was higher in specimens filled with cement MTA-based, Endo-C.P.M.- Sealer. ...
Institución
Universidade Federal do Rio Grande do Sul. Faculdade de Odontologia. Curso de Especialização em Endodontia.
Colecciones
-
Ciencias de la Salud (1492)
Este ítem está licenciado en la Creative Commons License