Show simple item record

dc.contributor.advisorMachado, Ivan Guerrapt_BR
dc.contributor.authorAndrade, Luís Gustavo Caldas dept_BR
dc.date.accessioned2018-04-05T02:25:45Zpt_BR
dc.date.issued2018pt_BR
dc.identifier.urihttp://hdl.handle.net/10183/174417pt_BR
dc.description.abstractA combinação entre excelentes propriedades mecânicas, facilidade de transformação, capacidade de deformação e oferta, faz do aço uma fonte de matéria prima ímpar à indústria de estruturas metálicas. Esta pesquisa estudou o comportamento de membros estruturais de aço soldados, submetidos a impacto de baixa velocidade. Os corpos de prova foram soldados à topo e ângulo, com metal base ASTM A-36 e metal de adição ER70S-6 e ER120S-G. Nos corpos de prova soldados à topo, avaliou-se a influência da adoção de consumível de baixa e alta resistência, além da influência do tratamento térmico de alívio de tensões sob as propriedades mecânicas da junta soldada. Nos perfis estruturais “I” e “T”, as variáveis utilizadas foram: o comprimento da viga, o consumível utilizado, o uso de filete de solda contínuo ou intermitente e a geometria do perfil. Para a realização dos ensaios, desenvolveu-se um martelo de queda com massa de 267 Kg e velocidade de impacto aos corpos de prova a 6,7 m/s Nos corpos de prova soldados à topo avaliou-se o percentual de fratura frágil e dureza no metal de solda, enquanto que, nos perfis “I” e “T” analisou-se a deflexão sofrida pela viga após o impacto, a dureza no metal de solda e a dureza na alma da viga. Ao término deste estudo, pôde-se observar que os espécimes soldados à topo apresentaram redução do percentual de fratura frágil somente para as temperaturas de tratamento térmico a 650 °C enquanto que, na temperatura de 500 °C observou-se aumento do percentual de fratura frágil e dureza no metal de solda. Nos perfis estruturais, quando da adoção de consumível de alta resistência, não houve influência na deflexão das vigas. Ao se comparar a deflexão dos perfis “I” vs perfis “T”, a deflexão dos perfis “I” em nenhum dos casos excedeu 1/3 da deflexão dos perfis “T”, demonstrando desempenho superior, mesmo ao se levar em conta o aumento de massa e consequente aumento de momento de inércia.pt_BR
dc.description.abstractThe conjunction of pristine mechanical properties, easiness in transformation, strain capability and offer, make steel a valuable raw material to the mechanical structures industry. This research studied the behavior of welded structural members, subjected to low-velocity impact. The test coupons were butt- and fillet welded (“T” and “I” profiles), and the base metal used was the ASTM A-36, and the filler metal adopted was ER70S-6 and ER120S-G. On the butt welded specimens, it was evaluated the influence of using a matching and over-matching filler metal, and the influence of postweld heat treatment on the welded joint’s mechanical properties. On the structural profiles (T- and I-beams) the variables used were: the beam length, filler metal used, continuous or intermittent fillet weld and the profile geometry (T or I). To perform the tests, a guided-fall hammer was built with a mass of 267 kg, hitting the specimens at 6,7 m/s. For the butt-welded specimens, the results were evaluated by brittle fracture percentage and weld metal hardness The “T” and “I” profiles were evaluated through deflection measurement, weld metal and web hardness. By the end of this study, it was observed that, for the but welded joints, only the heat treatment at 650 °C were effective, reducing the percentage of brittle fracture and hardness, while the 500 °C treatment increased the brittle fracture percentage and weld metal hardness. On the structural profiles, when adopting overmatching filler metal, there was no influence on beam deflection. When comparing I- and T-profiles deflections, the deflections of the first never exceed one third of the latter on, showing far superior performance, even when taking into account mass and consequently moment of inertia increase.en
dc.format.mimetypeapplication/pdf
dc.language.isoporpt_BR
dc.rightsOpen Accessen
dc.subjectWeldingen
dc.subjectEstruturas metálicaspt_BR
dc.subjectMetallic Structuresen
dc.subjectSoldagempt_BR
dc.subjectImpacto em estruturaspt_BR
dc.subjectStructural Impacten
dc.titleImpacto estrutural em membros soldados de açopt_BR
dc.typeDissertaçãopt_BR
dc.identifier.nrb001062124pt_BR
dc.degree.grantorUniversidade Federal do Rio Grande do Sulpt_BR
dc.degree.departmentEscola de Engenhariapt_BR
dc.degree.programPrograma de Pós-Graduação em Engenharia de Minas, Metalúrgica e de Materiaispt_BR
dc.degree.localPorto Alegre, BR-RSpt_BR
dc.degree.date2018pt_BR
dc.degree.levelmestradopt_BR