dc.description.abstractNeste trabalho, objetivou-se a síntese de zeólitas, pelo processo hidrotérmico em meio alcalino, utilizando como fonte alternativa de silício as cinzas volantes de carvão e a caracterização dos produtos obtidos. As variáveis estudadas foram a concentração de NaOH no meio reacional (0,23 ou 3,5 mol/L), o tempo de reação (1, 3 ou 6 dias) e a razão Si/Al no gel de síntese (1, 2, 3 ou 4). As cinzas de carvão, antes de serem utilizadas no processo, passaram por um processo de secagem em estufa a 110°C por 24 horas. Para a caracterização das cinzas foram realizados ensaios de difração e fluorescência de raios X, análise termogravimétrica e avaliação da distribuição granulométrica. As cinzas apresentaram como principais componentes SiO2 (68,43%), Al2O3 (14,77%) e Fe2O3 (7,91%), sendo 90% de suas partículas com diâmetro inferior a 119 m. A caracterização microestrutural das zeólitas obtidas foi feita por meio de microscopia eletrônica de varredura (MEV) e de transmissão (MET), da área superficial específica utilizando o método Brunauer-Emmet-Teller (BET) e difração de raio X (DRX). Tendo como base a caracterização das amostras, pode-se destacar que foram sintetizadas zeólitas com fase majoritária sodalita, além de quartzo e mulita como subprodutos. A microestrutura dos pós apresentou-se aglomerada com área superficial em torno de 10 m²/g. As zeólitas obtidas foram também avaliadas quanto à sua atividade fotocatalítica, degradando até 86% do corante utilizado em 60 minutos.pt_BR
dc.description.abstractThis study aimed to synthesized zeolites by hydrothermal process in alkaline medium, using coal fly ashes as an alternative source of silicon, and characterized their properties. The variables studied were the concentration of NaOH in the reaction medium (0.23 or 3.5 mol/L), reaction time (1, 3 or 6 days) and the Si/Al ratio in the synthesis gel (1, 2, 3 or 4). The coal ash was dried in an oven at 110°C for 24 hours before being used in the process. For the characterization of the ash analysis such as X-ray diffraction and fluorescence, thermosgravimetry and particle size distribution were performed. The ash presented as main components SiO2 (68.43%), Al2O3 (14.77%), Fe2O3 (7.91%), with 90% of its particles with diameter smaller than 119 μm. The microstructural characterization of the obtained zeolites was made by scanning and transmission electron microscopy, the specific surface area was calculated using the Brunauer-Emmet-Teller method (BET) and X-ray diffraction was used to characterize the constituent phases. The characterization of the samples showed that it were synthesized the zeolite type sodalite, and the presence of quartz and mullite was identified as by-products. The microstructure of the powders showed clusters with specific surface area of about 10 m²/g. The obtained zeolites were also evaluated considering their photocatalytic activity, degrading up to 86% of the dye used in 60 minutes.en
dc.format.mimetypeapplication/pdf
dc.language.isoporpt_BR
dc.rightsOpen Accessen
dc.subjectCinza de carvão : Caracterizaçãopt_BR
dc.subjectZeolitas : Síntesept_BR
dc.subjectFotocatálisept_BR
dc.titleSíntese e caracterização de zeólita tipo sodalita obtida a partir de cinzas volantes de carvão mineral utilizado na usina termoelétrica de Candiota-RSpt_BR
dc.typeDissertaçãopt_BR
dc.identifier.nrb000989043pt_BR
dc.degree.grantorUniversidade Federal do Rio Grande do Sulpt_BR
dc.degree.departmentEscola de Engenhariapt_BR
dc.degree.programPrograma de Pós-Graduação em Engenharia de Minas, Metalúrgica e de Materiaispt_BR
dc.degree.localPorto Alegre, BR-RSpt_BR
dc.degree.date2015pt_BR
dc.degree.levelmestradopt_BR


Files in this item

Thumbnail
   

This item is licensed under a Creative Commons License

Show simple item record