dc.description.abstractA armadura de tração de dutos flexíveis é a camada responsável por suportar as cargas axiais destes equipamentos em campo. Com a tendência de aumento das profundidades de exploração e produção de petróleo offshore, principalmente dos campos do pré-sal brasileiro, faz-se necessário o uso de materiais com desempenho superior. Este trabalho buscou avaliar e comparar dois aços de alta resistência mecânica para tal aplicação, um predominantemente perlítico e outro martensítico. Durante a vida em serviço destes componentes, eles sofrem tensões axiais cíclicas associadas ao processo de corrosão, que gera pites como concentradores de tensões. Considerando estes aspectos, os materiais foram avaliados segundo seu comportamento à fadiga sem e com a presença de um pequeno defeito conhecido, que atua como um entalhe e busca simular um pite de corrosão. Além disso, esses materiais foram caracterizados metalúrgica e mecanicamente e sua tenacidade à fratura foi estimada via o método do CTOD. A partir dos dados experimentais, foi quantificada a sensibilidade ao entalhe, guiada essencialmente pelo processo de iniciação de trinca, ao passo que a tenacidade à fratura não foi decisiva. O material martensítico apresentou desempenho superior em fadiga e menor sensibilidade ao entalhe e mostrou-se promissor para a aplicação como arame da armadura de tração.pt_BR
dc.description.abstractThe tensile armor of flexible pipes is the layer responsible for support axial loads of this equipment in field. With the trend of deep increase in offshore oil exploration and production, mainly in pre-salt fields, the use of materials with high performance becomes necessary. The aim of this dissertation is evaluate and compare two high strength steels for such application, one with perlite and other with martensitic matrix. During service life of these components, they are damaged by cyclic loading associated with corrosion process which promote corrosion pits like stress concentrators. Considering these aspects, the materials were evaluated according their fatigue behavior with and without a small defect that act as a notch and simulates a corrosion pit. In addition, they were characterized metallurgical and mechanically and their fracture toughness was estimated through CTOD test. From experimental data, notch sensitivity was quantified. This was driven by initiation process, and fracture toughness was not decisive. The martensitic material showed higher fatigue performance and lower notch sensitivity and presented itself promising for tensile armor wire application.en
dc.format.mimetypeapplication/pdf
dc.language.isoporpt_BR
dc.rightsOpen Accessen
dc.subjectFlexible pipeen
dc.subjectTubos flexíveispt_BR
dc.subjectAço de alta resistênciapt_BR
dc.subjectHigh strength steelsen
dc.subjectResistência à fraturapt_BR
dc.subjectFracture toughnessen
dc.subjectFatigueen
dc.subjectFadiga (Engenharia)pt_BR
dc.subjectNotch sensitivityen
dc.titleMateriais para aplicação em arames da armadura de tração de dutos flexíveis : comportamento frente a entalhespt_BR
dc.typeDissertaçãopt_BR
dc.identifier.nrb000984896pt_BR
dc.degree.grantorUniversidade Federal do Rio Grande do Sulpt_BR
dc.degree.departmentEscola de Engenhariapt_BR
dc.degree.programPrograma de Pós-Graduação em Engenharia de Minas, Metalúrgica e de Materiaispt_BR
dc.degree.localPorto Alegre, BR-RSpt_BR
dc.degree.date2015pt_BR
dc.degree.levelmestradopt_BR