Hardness evaluation, stoichiometry and grain size of titanium nitride obtained with plasma nitriding on Ti-6AI-4V samples
Fecha
2010Materia
Abstract
Titanium nitride films were formed on the surface of Ti-6Al-4V discs by plasma nitriding (glow discharge) in different N2:H2 atmospheres at several substrate temperatures. In this study the influence of the process parameters on dynamic micro-hardness were investigated. Grain sizes of the nitride films, determined with X-Ray Diffraction, were related to the nitriding parameters. TiNx stoichiometry was determined with Nuclear Reaction Analysis and showed a correlation to substrate temperature du ...
Titanium nitride films were formed on the surface of Ti-6Al-4V discs by plasma nitriding (glow discharge) in different N2:H2 atmospheres at several substrate temperatures. In this study the influence of the process parameters on dynamic micro-hardness were investigated. Grain sizes of the nitride films, determined with X-Ray Diffraction, were related to the nitriding parameters. TiNx stoichiometry was determined with Nuclear Reaction Analysis and showed a correlation to substrate temperature during the nitriding process. Micro-hardness measurements were taken on the nitrided surfaces. Grain sizes increased for a particular gas composition of 60%N2+40%H2 where hardness was lowest. ...
En
Revista Matéria. Rio de Janeiro: Coppe/UFRJ, 2010. Vol. 15, n. 2 (jun. 2010), p. 299-302
Origen
Nacional
Colecciones
-
Artículos de Periódicos (39774)Ciencias Exactas y Naturales (6068)
Este ítem está licenciado en la Creative Commons License