Controlled rotation of the exchange-bias direction in IrMn/Cu/Co via ion irradiation
Visualizar/abrir
Data
2008Autor
Tipo
Assunto
Abstract
Co/Cu/IrMn films were irradiated with 40 keV He+ ions varying the fluence and the current, with magnetic field applied at 120° with respect to the original exchange-bias direction. The angular variations of the exchange-bias field of the irradiated samples were compared with those of the as-made and the thermally annealed films. Gradual deviation of the exchange-bias direction with the fluence increase was observed. Complete reorientation of the easy axes of both ferromagnet and antiferromagnet ...
Co/Cu/IrMn films were irradiated with 40 keV He+ ions varying the fluence and the current, with magnetic field applied at 120° with respect to the original exchange-bias direction. The angular variations of the exchange-bias field of the irradiated samples were compared with those of the as-made and the thermally annealed films. Gradual deviation of the exchange-bias direction with the fluence increase was observed. Complete reorientation of the easy axes of both ferromagnet and antiferromagnet toward that of the field applied during irradiation was achieved for fluences higher than 1 1015 ions/cm2, accompanied with a significant enhancement of the exchange-bias field. ...
Contido em
Applied physics letters. New York. Vol. 93, no. 4 (July 2008), 042501, 3 p.
Origem
Estrangeiro
Coleções
-
Artigos de Periódicos (40361)Ciências Exatas e da Terra (6164)
Este item está licenciado na Creative Commons License