Exchange-diffusion reactions in HfSiON during annealing studied by Rutherford backscattering spectrometry, nuclear reaction analysis and narrow resonant nuclear reaction profiling
Fecha
2004Autor
Materia
Abstract
HfSiON films deposited on Si (001) by reactive sputtering were submitted to rapid thermal annealing at 1000 °C in vacuum, N2 and O2 atmospheres. The stability of the dielectric was evaluated by measuring the atomic transport and exchange of the chemical species, using Rutherford backscattering spectrometry, nuclear reaction analysis and narrow resonant nuclear reaction profiling. Annealing in O2 ambient reduced the N concentration mainly from near-surface regions where oxygen was incorporated i ...
HfSiON films deposited on Si (001) by reactive sputtering were submitted to rapid thermal annealing at 1000 °C in vacuum, N2 and O2 atmospheres. The stability of the dielectric was evaluated by measuring the atomic transport and exchange of the chemical species, using Rutherford backscattering spectrometry, nuclear reaction analysis and narrow resonant nuclear reaction profiling. Annealing in O2 ambient reduced the N concentration mainly from near-surface regions where oxygen was incorporated in comparable amounts. Vacuum annealing, on the other hand, induced N loss preferentially from the Si/dielectric interface and O loss preferentially from near-surface regions. The results are explained in terms of exchange-diffusion reactions occurring in the HfSiON. ...
En
Applied physics letters. Melville. Vol. 85, no. 19 (Nov. 2004), p. 4460-4462
Origen
Estranjero
Colecciones
-
Artículos de Periódicos (40021)Ciencias Exactas y Naturales (6101)
Este ítem está licenciado en la Creative Commons License