dc.description.abstractNo presente trabalho, é avaliada a aplicabilidade da eletrocoagulação como meio de tratamento de um efluente bruto de lubrificante de forjaria com 14% de óleo. Para tanto, foram testados aço comum e alumínio como materiais dos eletrodos, tipos de montagem do sistema (tanto monopolar quanto bipolar) e quantidades diferentes de eletrodos – 2 e 6 eletrodos. Uma vez que a condutividade do efluente era baixa, menor do que 3 mS/cm) foi utilizado NaCl como eletrólito suporte nas seguintes concentrações: 1; 2; 4; 8 e 10 g/L. Para determinar a melhor dosagem do metal do eletrodo, foram aplicadas diferentes correntes que resultaram nas densidades de corrente de 47; 94 e 188 mA/cm2. Para este sistema em escala de laboratório, o ganho de tempo de processo com o uso de 6 eletrodos não foi significativo quando comparado com o sistema de 2 eletrodos devido ao seu maior gasto energético. Nos experimentos realizados, a maior densidade de corrente aplicada resultou em melhores taxas de remoção de DQO e COT, provavelmente devido à maior quantidade de alumínio disponível para formar agentes coagulantes. Foi possível utilizar, a técnica, que é comumente utilizada em efluentes com condutividade moderada a alta em um efluente com baixa condutividade e quebrar a emulsão, separando o grafite em todos os experimentos realizados. Além disso todas as condições testadas apresentaram redução da DQO acima de 90%. Os parâmetros operacionais que proporcionaram os melhores resultados foram distância entre os eletrodos de 10 mm, concentração de NaCl igual a 8 g/L e densidade de corrente de 188 mA/cm2.pt_BR
dc.description.abstractIn the present study the applicability of electrocoagulation (EC) as treatment process for a forging lubricant effluent with 14% of oil was investigated. In order to do this, plain carbon steel and aluminum were tested as electrode material, system arrangements types (monopolar and bipolar) and different electrode quantities – 2 and 6. Once the effluent conductivity was low (less than 3 mS/cm), NaCl was used as supporting electrolyte in the following concentrations: 1; 2; 4; 8 e 10 g/L. In order to determine the best metal dose, different currents were applied which resulted in current densities of 47; 94 and 188 mA/cm2. To this bench scale system, the improvements in process duration using 6 electrodes instead of 2 was not significant because of its energy consumption is much higher. In these experiments, the higher current density resulted in the best removal rated of COD and TOC, probably due to higher aluminum availability to form precipitates. It was possible to use a technique, which is commonly used in aqueous effluents that have medium to high conductivity, on an effluent with low conductivity in order to break the emulsion and separate the graphite. This result was achieved in all the experiments carried out, besides that, all the tested conditions presented a COD reduction higher than 90%. The operational parameters that have given the best results were electrode distance of 10 mm, NaCl concentration of 8 g/L and current density equal to 188 mA/cm2.en
dc.format.mimetypeapplication/pdf
dc.language.isoporpt_BR
dc.rightsOpen Accessen
dc.subjectGrafitept_BR
dc.subjectTratamento de efluentes industriaispt_BR
dc.subjectEletrocoagulaçãopt_BR
dc.titleRemoção de grafite de um efluente oleoso através de técnicas eletroquímicaspt_BR
dc.typeTesept_BR
dc.contributor.advisor-coBernardes, Andrea Mourapt_BR
dc.identifier.nrb000981234pt_BR
dc.degree.grantorUniversidade Federal do Rio Grande do Sulpt_BR
dc.degree.departmentEscola de Engenhariapt_BR
dc.degree.programPrograma de Pós-Graduação em Engenharia de Minas, Metalúrgica e de Materiaispt_BR
dc.degree.localPorto Alegre, BR-RSpt_BR
dc.degree.date2014pt_BR
dc.degree.leveldoutoradopt_BR


Ficheros en el ítem

Thumbnail
   

Este ítem está licenciado en la Creative Commons License

Mostrar el registro sencillo del ítem