Tailoring coercivity of unbiased exchange-coupled ferromagnet/antiferromagnet bilayers
Visualizar/abrir
Data
2012Autor
Tipo
Assunto
Abstract
This paper reports experimental results obtained on unconventional exchange-coupled ferromagnet/ antiferromagnet (FM/AF) system showing zero net bias. The Curie temperature of the FM (NiCu) is lower than the blocking temperature of the AF (IrMn). Samples were either annealed or irradiated with He, Ar, or Ge ions at 40 keV. Due to the exchange coupling at the FM/AF interface, the coercivity (HC) of the as-deposited FM/AF bilayer is rather higher than that of the corresponding FM single layer. We ...
This paper reports experimental results obtained on unconventional exchange-coupled ferromagnet/ antiferromagnet (FM/AF) system showing zero net bias. The Curie temperature of the FM (NiCu) is lower than the blocking temperature of the AF (IrMn). Samples were either annealed or irradiated with He, Ar, or Ge ions at 40 keV. Due to the exchange coupling at the FM/AF interface, the coercivity (HC) of the as-deposited FM/AF bilayer is rather higher than that of the corresponding FM single layer. We found that by choosing a proper ion fluence or annealing temperature, it is possible to controllably vary HC. Ion irradiation of the FM single layer has lead to only a decrease of HC and annealing or He ion irradiation has not caused important changes at the FM/AF interface; nevertheless, a twofold increase of HC was obtained after these treatments. Even more significant enhancement of HC was attained after Ge ion irradiation and attributed to ion-implantation-induced modification of only the FM layer; damages of the FM/AF interface, on the other hand, decrease the coercivity. ...
Contido em
Journal of applied physics. New York. Vol. 112, no. 1 (July 2012), 013904, 5 p.
Origem
Estrangeiro
Coleções
-
Artigos de Periódicos (39774)Ciências Exatas e da Terra (6068)
Este item está licenciado na Creative Commons License