Avaliação da penetrabilidade dentinária apical dos cimentos AH Plus e MTA Fillapex por meio da microscopia confocal
dc.contributor.advisor | Só, Marcus Vinicius Reis | pt_BR |
dc.contributor.author | Baldissera, Renata dos Santos | pt_BR |
dc.date.accessioned | 2013-11-05T01:57:40Z | pt_BR |
dc.date.issued | 2013 | pt_BR |
dc.identifier.uri | http://hdl.handle.net/10183/79931 | pt_BR |
dc.description.abstract | O objetivo desse trabalho foi analisar comparativamente, por meio da microscopia confocal de varredura à laser (MCVL), a penetrabilidade de dois cimentos endodônticos à base de resina, na dentina radicular do terço apical, de dentes humanos. Trinta e dois dentes humanos foram distribuídos em dois grupos experimentais de 15 dentes cada e 02 controles: Grupo MTAF- os canais radiculares foram obturados pela técnica de condensação lateral da guta-percha e cimento à base de resina de salicilato (MTA Fillapex, Angelus, Londrina, PR); Grupo AHP- técnica da condensação lateral da guta percha e cimento à base resina epóxica AH Plus (Dentsply-Maillefer, Ballaigues, Suiça); dois dentes não foram obturados e serviram como controle. Previamente à obturação, o corante Rhodamina B foi acrescentado aos cimentos, em uma proporção de 0,1%, para proporcionar fluorescência. As amostras foram armazenadas em 100% de umidade a 37ºC por 1 semana e após, seccionadas horizontalmente a 2mm do ápice radicular e visualizadas através da MCF. A área de penetração dos cimentos endodônticos dentro dos túbulos dentinários, foi mensurada através do programa Adobe Photoshop( CS6 versão13.0) e posteriormente convertida em porcentagem de área. Não houve diferenças significativas entre os dois grupos experimentais (P = 0,8195). O MTA Fillapex e o AH Plus apresentaram similar penetração nos túbulos dentinários a despeito das suas diferentes composições químicas. | pt_BR |
dc.description.abstract | The aim of this study was to assess the penetrability of two resin-based sealers into dentin tubules using confocal laser scanning microscopy (CLSM). Thirty-two human teeth were divided in two groups (N = 15): MTAF group – canals were filled by lateral compaction and salicylate resin-based sealer (MTA Fillapex, Angelus, Londrina, Brazil); AHP group – canals were filled by lateral compaction and epoxy resin-based sealer AH Plus (Dentsply-Maillefer, Ballaigues, Switzerland). Two teeth were not filled and served as control. Previous to the root canal filling, Rhodamine B dye was mixed with the sealers in a ratio of 0.1% in order to provide fluorescence. For CLSM the samples were stored at 100% humidity and 37°C for one week and then transversally sectioned at 2mm from the apex. The sealer penetrability was measured using Adobe Photoshop software. The area of penetration of sealers into dentinal tubules was measured using the program Adobe Photoshop and then converted to percentage of the area. Both sealers penetrate into dentin tubules. The test did not reveal differences between the two experimental groups (P = 0.8195). MTA Fillapex and AH Plus presented similar penetrability into dentin tubules besides their different chemical composition. | en |
dc.format.mimetype | application/pdf | |
dc.language.iso | por | pt_BR |
dc.rights | Open Access | en |
dc.subject | Endodontics | en |
dc.subject | Endodontia | pt_BR |
dc.subject | Confocal laser scanning microscopy | en |
dc.subject | Cimentos | pt_BR |
dc.subject | Filling root canal | en |
dc.title | Avaliação da penetrabilidade dentinária apical dos cimentos AH Plus e MTA Fillapex por meio da microscopia confocal | pt_BR |
dc.type | Trabalho de conclusão de especialização | pt_BR |
dc.identifier.nrb | 000902539 | pt_BR |
dc.degree.grantor | Universidade Federal do Rio Grande do Sul | pt_BR |
dc.degree.department | Faculdade de Odontologia | pt_BR |
dc.degree.local | Porto Alegre, BR-RS | pt_BR |
dc.degree.date | 2013 | pt_BR |
dc.degree.level | especialização | pt_BR |
dc.degree.specialization | Curso de Especialização em Endodontia | pt_BR |