dc.description.abstractElastômeros termoplásticos vulcanizados, TPVs, à base de co-poliamida (PA6,6-6) e borracha nitrílica (NBR), foram preparados por vulcanização dinâmica em câmara de mistura a partir de um sistemas de vulcanização tendo como componente principal o peróxido de dicumila e os coagentes bismaleimida e enxofre. Variando-se a proporção dos componentes, estudou-se a influência do enxofre sobre as propriedades mecânicas e deformação permanente à compressão. A morfologia foi determinada por análise de microscopia eletrônica de varredura. Todos os TPVs apresentam propriedades mecânicas superiores à blenda PA/NBR correspondente. TPVs com domínios elastoméricos da ordem de 5 µm foram obtidos com o sistema de reticulação constituído de peróxido de dicumila/bismaleimida/enxofre (DCP/BMI/S) na proporção de 2,4/0,4/0,7 php, independentemente da forma de apresentação da NBR (compacta ou pó). Estes materiais apresentaram excelente desempenho mecânico alcançando-se tensões de ruptura da ordem de 20 MPa. A presença do enxofre conferiu propriedades mecânicas particulares aos TPVs. Para todos os sistemas de reticulação, os TPVs apresentaram boa resistência química em solventes apolares (iso-octano e óleo 20W50), atribuída à natureza química do par PA/NBR, e valores similares para a deformação permanente à compressão.pt_BR
dc.description.abstractThermoplastic vulcanizates (TPVs) based on polyamide (PA6,6-6) and nitrile rubber (NBR) were prepared by dynamic vulcanization in an internal mixer based on a mixed curing system having dicumyl peroxide as the main component and bismaleimide and sulfur as coagents. The proportion of the components as well as the influence of the sulfur content on the mechanical properties and compression set were studied. The morphologies were determined by scanning electronic microscopy. All the TPVs exhibit better properties than the blend. Elastomeric domains of ca. 5 µm were obtained for the curing system dicumyl peroxide/bismaleimide/sulfur (DCP/BMI/S) in a proportion of 2.4/0.4/0.7 php, independently of the form of the NBR (crumb or powder). These materials showed excellent mechanical properties, reaching a tension of rupture of about 20 MPa. The use of sulfur as curing co-agent gives the material unique properties. All the TPVs exhibited good resistance to non polar solvents (isooctane and oil 20W50) and similar values for the compression set.en
dc.format.mimetypeapplication/pdf
dc.language.isoporpt_BR
dc.relation.ispartofPolímeros (São Carlos): ciência e tecnologia. São Carlos, SP. Vol. 22, no. 2 (abr./jun. 2012), p. 206-212pt_BR
dc.rightsOpen Accessen
dc.subjectThermoplastic vulcanizatesen
dc.subjectElastômeros termoplásticospt_BR
dc.subjectPeróxido de dicumilapt_BR
dc.subjectCrosslinking by dicumyl peroxideen
dc.subjectCuring coagentsen
dc.subjectBorracha nitrílicapt_BR
dc.subjectMorphology of PA/NBRen
dc.titleTPVs PA/NBR : sistema de reticulação e propriedadespt_BR
dc.title.alternativePA/NBR TPVs : crosslink system and propertiesen