dc.description.abstractO presente trabalho estuda uniões entre chapas de aço DP600 e chapas das ligas de alumínio AA 6181–T4 e AA 5754–H22, obtidas através do processo Friction Spot Welding (FSpW). A soldagem de materiais dissimilares é um dos grandes desafios para a engenharia, pois as propriedades de distintos materiais são muito diferentes na maioria das vezes, o que dificulta a realização deste tipo de união pelos métodos convencionais de soldagem com fusão. O processo FSpW requer menos energia que os processos de soldagem convencionais, não produz fumos, radiação ou resíduos. Permite obter a união de materiais no estado sólido, sendo, portanto potencialmente indicado para uniões dissimilares. Por ser um processo muito mais “limpo” que os usados convencionalmente, pode contribuir significativamente com uma grande preocupação mundial que é a sustentabilidade. A influência de um revestimento galvanizado nas chapas de aço para a qualidade das uniões resultantes foi avaliada realizando-se as operações de soldagem com as chapas de aço nas condições com e sem a camada galvanizada. O método estatístico de Taguchi foi utilizado para definir os parâmetros de soldagem que maximizassem a resistência das juntas para cada condição de ensaio, sendo a qualidade das juntas obtidas definida pela resistência da união ao ensaio de cisalhamento. Durante a soldagem, a temperatura em pontos específicos foi adquirida e, posteriormente, as juntas foram submetidas à análise metalográfica e de composição química por EDS. A partir da análise das macro e microestruturas dos corpos de prova com melhor resistência ao cisalhamento, foi possível associar diferentes parâmetros de processo e mecanismos de união para cada tipo de junta. O estudo comprovou a possibilidade de obtenção de uniões dissimilares entre o aço e as duas ligas de alumínio através do processo FSpW, especialmente quando utilizou-se o aço com a camada galvanizada que apresentou modo de união mais eficaz.pt_BR
dc.description.abstractThis work aims at the study of welding DP600 steel to AA6181-T4 and AA5754-H22 aluminum alloys plates by Friction Spot Welding (FSpW). Welding of dissimilar materials is a great challenge for engineering due to the diverse properties of different materials, that difficult welding by conventional methods of fusion. FSpW is a joining method that requires lower energy than conventional welding processes and produces no hazard gases or radiation. It allows solid state joining that is potentially indicated to dissimilar materials joining, and contributes significantly to sustainability, because the process can be considered “cleaner” that those used conventionally. The influence of the galvanized layer on the joint performance with the steel plates on was tested using steel plates with and without this coating. The Taguchi statistic method was employed to define the welding process parameters that produce higher shear stress resistance to each test condition, so the welding joints quality was defined based on the union resistance to shear. During the welding operation the temperature at given positions was acquired and the resulting joints were submitted to metallographic and chemical composition analysis. From the analysis of specimen that showed best stress test performance to each joint condition, it was possible to associate different process parameters and joint mechanisms to each condition. The study demonstrates the feasibility of joining the steel to both aluminum alloys using FSpW. The best shear test results were obtained with the presence of a galvanized layer.en
dc.format.mimetypeapplication/pdf
dc.language.isoporpt_BR
dc.rightsOpen Accessen
dc.subjectJoining of dissimilar materialsen
dc.subjectSoldagem por fricçãopt_BR
dc.subjectAlumíniopt_BR
dc.subjectAluminium-steel weldingen
dc.subjectFriction spot weldingen
dc.subjectAçopt_BR
dc.subjectFSpWen
dc.titleEstudo de uniões dissimilares alumínio-soldas por "Solda Ponto por Fricção e mistura mecânica com preenchimento do furo" (Friction Spot Welding - FSpW)pt_BR
dc.typeTesept_BR
dc.identifier.nrb000864126pt_BR
dc.degree.grantorUniversidade Federal do Rio Grande do Sulpt_BR
dc.degree.departmentEscola de Engenhariapt_BR
dc.degree.programPrograma de Pós-Graduação em Engenharia Mecânicapt_BR
dc.degree.localPorto Alegre, BR-RSpt_BR
dc.degree.date2012pt_BR
dc.degree.leveldoutoradopt_BR


Ficheros en el ítem

Thumbnail
   

Este ítem está licenciado en la Creative Commons License

Mostrar el registro sencillo del ítem