dc.description.abstractNeste trabalho foi estudada a síntese de nanocompósitos de polietileno com crisotila original ou modificada. A crisotila foi tratada por três métodos distintos: Método A – aquecimento a 800 °C; Método B – lixiviação pela adição de ácido clorídrico 3 mol/L; Método C – lixiviação com ácido clorídrico 0,1 mol/L. As crisotilas foram caracterizadas por MEV-EDS, MET, DRX e DRIFTS. Após o tratamento térmico da crisotila a 800 °C, sua estrutura tornou-se totalmente disforme e aglomerada. Isto é justificado pela perda dos grupos OH de sua superfície. No método B, ocorreu à eliminação da camada de brucita pelo lixiviamento ácido, transformando a crisotila em uma sílica amorfa. No método C, observou-se uma estrutura de nanotubos similar ao da crisotila pura, indicando poucas alterações após o tratamento com ácido diluído. Os nanocompósitos sintetizados via polimerização in situ foram obtidos em todos os métodos estudados. Estas polimerizações apresentaram boas atividades catalíticas e as temperaturas de degradação dos nanocompósitos foram próximas ou superiores ao do polietileno puro. As imagens de MEV mostraram que os polímeros sintetizados ficaram mais fibrosos com a adição de crisotila. Através das micrografias de MET observou-se uma boa dispersão da nanocarga na matriz polimérica em nanocompósitos obtidos por uso de catalisador suportado.pt_BR
dc.description.abstractIn this work was studied the synthesis of polyethylene/chrysotile nanocomposites obtained with neat or modified chrysotile. The chrysotile was treated by three different methods: Method A - heating till 800 ° C; Method B – treated with hydrochloric acid 3 mol/L; Method C - treated with hydrochloric acid 0.1 mol/L. The treated chrysotiles were characterized by SEM-EDS, TEM, XRD and DRIFTS. The thermal treatment of the chrysotile at 800 °C, produced a shapeless and aggregated material obtained by the loss of OH groups. In method B, the brucite layer was removed by the concentrated acid, transforming chrysotile into amorphous silica. In the method C, verified a structure similar to the nanotubes of neat chrysotile, indicating little change after less concentrated acid treatment. The nanocomposites synthesized via in situ polymerization were obtained in all methods. These polymerizations showed good catalytic activities and the nanocomposites obtained higher degradation temperature than pure polyethylene. SEM images showed that the polymers became more fibrous with the addition of chrysotile. By the TEM micrographs it was observed a good dispersion of nanoparticles in the polymer matrix in nanocomposites by using supported catalyst.en
dc.format.mimetypeapplication/pdf
dc.language.isoporpt_BR
dc.rightsOpen Accessen
dc.subjectNanocompósitospt_BR
dc.subjectPolimerização in situpt_BR
dc.subjectPolietilenopt_BR
dc.subjectCrisotilapt_BR
dc.subjectPolímerospt_BR
dc.titleNanocompósitos de polietileno/crisotila por polimerização in situpt_BR
dc.typeDissertaçãopt_BR
dc.identifier.nrb000771913pt_BR
dc.degree.grantorUniversidade Federal do Rio Grande do Sulpt_BR
dc.degree.departmentInstituto de Químicapt_BR
dc.degree.programPrograma de Pós-Graduação em Químicapt_BR
dc.degree.localPorto Alegre, BR-RSpt_BR
dc.degree.date2010pt_BR
dc.degree.levelmestradopt_BR


Ficheros en el ítem

Thumbnail
   

Este ítem está licenciado en la Creative Commons License

Mostrar el registro sencillo del ítem