dc.description.abstractObjetivos: Avaliar a influência do BIO-C TEMP na penetrabilidade intratubular através da microscopia confocal de varredura a laser (MCVL) e resistência de união (push-out)dos cimentos de resina epóxi (AH Plus- AH) e biocerâmico (BIO-C SEALER-BC), e avaliar a superfíciedentinária após a remoção da medicação através da microscopia eletrônica de varredura (MEV). Material e Método: Foram utilizados 53 incisivos bovinos, 48 foram obturados com dois cimentos diferentes (AH Plus e BIO-C SEALER). Os grupos foram estabelecidos pelo tipo decimento utilizado e tempo de medicação intracanal(MIC), a saber:BC 0BT, BC 7 BT,BC 30 BT, AP 0 BT, AP 7 BT, AP 30 BT. Para avaliação em MEV foram utilizados 5 dentes não obturados:BT 0, BT 7d, BT 30d. Para os dados de resistência de união foram realizados os testes estatísticos de Kruskal-Wallis e teste T para comparações dos cimentos nos diferentes tempos experimentais e dentro do mesmo tempo experimental, respectivamente; distribuição de frequências absolutas para análise dos padrões de falha; e uma análise descritiva dos fenômenosobservados em MCVL e MEV. Resultados: Bio C Temp diminuiu a força de união do AP e BC em ambos os tempo experimentais (7 e 30 dias) (P< 0.05). Quando o terço radicular foi considerado, somente no terço médio ocorreu uma diminuição significativa na força de união entre AP O BT e AP 7 BT, assim como, entre BC 0 BT e BC 30 BT, e entre BC 7 BT e BC 30 BT (P< 0.05). O cimento AH Plus mostrou diferenças significativas nos valores de resistência de união quando comparados ao período em que não foi utilizada a medicação BIO-C TEMP e o período de 7 dias em que foi usada tal medicação (P< 0,05). Não houve diferenças entre os cimentos endodônticos dentro de cada terço radicular e de cada tempo experimental (P> 0,05). A penetração intratubular do AH Plus foi maior do que a do BIO-C SEALER. Com a MEV foi possível observar remanescentes da pasta biocerâmica sobre a superfície dentinária em ambos os grupos (7 e 30 dias). Conclusão: BIO-C TEMP diminuiu a resistência de união em ambos os gruposobservados.pt_BR
dc.description.abstractObjectives: The aim of this study was to evaluate the influence of BIO-C TEMP (BT) on intratubular penetrability through confocal laser scanning microscopy (CLSM) and bond strength (push out)of epoxy resin (AH Plus- AP) and bioceramic (BIO-C SEALER - BC) sealers and evaluate the dentin surface after removing the root canal dressing by scanning electron microscopy (SEM). Materials and Methods: Fifty- three bovine incisors were used, forty-eight were filled with two different sealers. The groups were established by the type of sealer used and root canal dressing use, namely: BC 0 BT, BC 7 BT, BC 30 BT, AP 0 BT, AP 7 BT, AP 30 BT. For SEM evaluation, five unfilled teeth were used: BT 0, BT 7d, BT 30d. For the bond strength data, the Kruskal-Wallis statistical tests and T test were performed for comparisons of sealers at different experimental times and within the same experimental time respectively, distributionof absolute frequencies for analysis of failure patterns, and a descriptive analysis in CLSM and SEM. Results: Bio C Temp decreased the bond strength of AH Plus sealer and Bio C Sealer in both experimental times (7 and 30 days) (P< 0.05). When the root third was considered, only in the middle third occurred a significant decrease in the bond strength between AP O BT and AP 7 BT, as well as, between BC 0 BT and BC 30 BT, and between BC 7 BT and BC 30 BT (P< 0.05). There were no significant differences in the intra-thirds root analysis (P > 0.05). The intratubular penetration with AP was higher when compared to the BC. SEM showed remnants of BT on the dentin surface in both groups (7 and 30 days). Conclusion: BT decreased bondstrength in both groups studied.en
dc.format.mimetypeapplication/pdfpt_BR
dc.language.isoporpt_BR
dc.rightsOpen Accessen
dc.subjectRoot canal dressingen
dc.subjectCerâmicapt_BR
dc.subjectBioceramicen
dc.subjectMicroscopia eletrônica de varredurapt_BR
dc.subjectMicroscopia confocalpt_BR
dc.subjectScanning electron microscopyen
dc.subjectPreparações farmacêuticas odontológicaspt_BR
dc.subjectLaser scanning confocal microscopyen
dc.subjectSealeren
dc.titleMedicação intracanal biocerâmica e sua influência na penetração intratubular e força de união de cimentos endodônticospt_BR
dc.title.alternativeBioceramic root canal dressing and its influence on intratubular penetration and bonding strenght of endodontic sealers en
dc.typeDissertaçãopt_BR
dc.identifier.nrb001209284pt_BR
dc.degree.grantorUniversidade Federal do Rio Grande do Sulpt_BR
dc.degree.departmentFaculdade de Odontologiapt_BR
dc.degree.programPrograma de Pós-Graduação em Odontologiapt_BR
dc.degree.localPorto Alegre, BR-RSpt_BR
dc.degree.date2024pt_BR
dc.degree.levelmestradopt_BR


Ficheros en el ítem

Thumbnail
   

Este ítem está licenciado en la Creative Commons License

Mostrar el registro sencillo del ítem