Influência da adiçao de alfa-fosfato tricálcico (α -TCP) e brometo de miristil trimetil amônio (MYTAB) nas propriedades de uma resina composta experimental
Fecha
2023Nivel académico
Doctorado
Tipo
Otro título
Influence of addition of alpha-tricalcium phosphate (α -tcp) and myristyl trimethyl ammonium bromide (mytab) on the properties of an experimental composite resin
Materia
Resumo
O objetivo do estudo foi desenvolver uma resina composta com a incorporação de Alfa fosfato tricálcico (a-TCP) e o Brometo de miristiltrimetilamônio (MYTAB) e avaliar suas propriedades remineralizantes e antimicrobianas, assim como as físicas, químicas e biológicas. La resina composta experimental foi (GMYTAB+a-TCP) elaborada a base de BisGMA (75 wt%), TEDGMA (25 wt%), TPO (fotoiniciador), BHT (inibidor) e como carga vidro de bário e sílica coloidal. Um grupo sem a adição desses compostos foi u ...
O objetivo do estudo foi desenvolver uma resina composta com a incorporação de Alfa fosfato tricálcico (a-TCP) e o Brometo de miristiltrimetilamônio (MYTAB) e avaliar suas propriedades remineralizantes e antimicrobianas, assim como as físicas, químicas e biológicas. La resina composta experimental foi (GMYTAB+a-TCP) elaborada a base de BisGMA (75 wt%), TEDGMA (25 wt%), TPO (fotoiniciador), BHT (inibidor) e como carga vidro de bário e sílica coloidal. Um grupo sem a adição desses compostos foi usado como controle (GCtrl). Os testes realizados foram: grau de conversão (n=3), resistencia flexural (n=6), microdureza e amolecimento em solvente (n=3), deposição mineral (n=3), citotoxicidade (n=5) e atividade antimicrobiana (n=3). O cálculo amostral foi realizado com um programa de análise estatística para um nível de significância de 0.05% e um poder de estudo de 80%.A normalidade dos valores foi testada por meio do teste Shapiro-Wilk. Não houve diferença entre os grupos para o grau de conversão (67.08% (±7.25) para o GCtrl e 60.41% (±1.10) para o GMYTAB+a-TCP) e a resistência à flexão (65.60 (±2.90) MPa para o GMYTAB+a-TCP e 40.61 (±2.15) Mpa para o GCtrl. O grupo experimental (GMYTAB+a-TCP) apresentou maior percentagem de degradação depois da imersão em solvente (25.49 (±2.14) para o GCtrl. e 12.17 (±3.11) % para o GMYTAB+a-TCP. Menor viabilidade celular (91.44 (±10.22)% para o GCtrl e 43.33 (±4.98)% para o GMYTAB+a-TCP) e uma maior redução na viabilidade bacteriana em biofilme e análise planctónica foi observada para o grupo GMYTAB+a-TCP. A deposição mineral aumentou após a imersão dos espécimes em SBF. Concluiu-se que a incorporação de MYTAB+a-TCP numa resina composta pode melhorar suas propriedades físicas, químicas e biológicas, e pode ser uma estratégia promissora para promover remineralização terapêutica e atividade antibacteriana na interface resina composta-dente. ...
Abstract
The aim of this study was to evaluate the potential capability of an experimental composite resin with the addition of Myristyltrimethylammonium bromide (MYTAB) and Αlfa-Tricalcium Phosphate (α-TCP) as antibacterial and remineralizing effect. The physical, chemical, and biological properties of its incorporation on the material were also explored. The experimental composite resin (GMYTAB+a-TCP) was formulated mixing Bisphenol A-Glycidyl Methacrylate (BisGMA-75 wt%), Triethylene Glycol Dimethacr ...
The aim of this study was to evaluate the potential capability of an experimental composite resin with the addition of Myristyltrimethylammonium bromide (MYTAB) and Αlfa-Tricalcium Phosphate (α-TCP) as antibacterial and remineralizing effect. The physical, chemical, and biological properties of its incorporation on the material were also explored. The experimental composite resin (GMYTAB+a-TCP) was formulated mixing Bisphenol A-Glycidyl Methacrylate (BisGMA-75 wt%), Triethylene Glycol Dimethacry late (TEGDMA-25 wt%), and a photoinitiator system, Trimethyl benzoyldiphenylphosphine oxide (TPO). As polymerization inhibitor, butylated hydroxytoluene (BTH) was added. Silica and barium glass were added as a filler. A group without the addition of these compounds was used as a control (GCtrl). The test performed were: degree of conversion (n=3), flexural strength (n=6), microhardness and softening in solvent (n=3), mineral deposition (n=3), cytotoxicity (n=5) and antimicrobial activity (n=3). A data was analyzed by the Shapiro-Wilk test. Student´s T-Test for independent specimens was used to compare differences between groups in the degree of conversion, flexural strength, cytotoxicity, KHN1, and ∆KHN%. Difference between KHN1 and KHN2 in each group were assessed by the Students T-Test. Descriptive analysis was performed for mineral deposition result. All tests were performed at a 5% significance level. There was no difference between groups for the degree of conversion (67.08% (±7.25) for (GCtrl) and 60.41% (±1.10) for (GMYTAB+a-TCP) and flexural strength (65.60 (±2.90) MPa for GMYTAB+a-TCP and 40.61 (±2.15) Mpa for GCtrl. The experimental group (GMYTAB+a-TCP) showed a higher percentage of degradation after immersion in solvent (25.49 (±2.14) for GCtrl. and 12.17 (±3.11) % for GMYTAB+a-TCP. Lower cell viability (91.44 (±10.22)% for GCtrl and 43.33 (±4.98)% for GMYTAB+a-TCP) and a greater reduction in bacterial viability in biofilme and planktonic analysis was observed for the GMYTAB+a-TCP group. Mineral deposition increased after specimens were immersed in SBF. Incorporation of MYTAB+a-TCP into composite resin can improve their physical, chemical and biological properties and may be promising strategy to achieve therapeutic remineralization and antibacterial activity at the composite-teeth interface. ...
Institución
Universidade Federal do Rio Grande do Sul. Faculdade de Odontologia. Programa de Pós-Graduação em Odontologia.
Colecciones
-
Ciencias de la Salud (9011)Odontología (746)
Este ítem está licenciado en la Creative Commons License