Waste glass in porcelain
Visualizar/abrir
Data
2005Tipo
Assunto
Abstract
In this work, the feldspar used as a flux in typical porcelain was replaced by waste glass, and the resulting batch composition contained 50% kaolin, 25% quartz and 25% waste glass. The properties of this porcelain with glass powder (GP) were compared to traditional porcelain (TP), which utilizes feldspar. The samples were fired at different temperatures, ranging from 1200 °C to 1400 °C. Technical parameters, such as water absorption, modulus of rupture and K IC, phase analysis by XRD, and micr ...
In this work, the feldspar used as a flux in typical porcelain was replaced by waste glass, and the resulting batch composition contained 50% kaolin, 25% quartz and 25% waste glass. The properties of this porcelain with glass powder (GP) were compared to traditional porcelain (TP), which utilizes feldspar. The samples were fired at different temperatures, ranging from 1200 °C to 1400 °C. Technical parameters, such as water absorption, modulus of rupture and K IC, phase analysis by XRD, and microstructure by SEM were analysed. The results indicated that the lower fracture toughness and MOR of GP is a consequence of the peculiar microstructure of this porcelain. The reduction in firing temperature and the use of a cheaper substitute for feldspar makes GP also an attractive economical alternative. ...
Contido em
Materials research : revista ibero-americana de materiais. São Carlos, SP. vol. 8, no. 1 (jan.- mar. 2005), p. 39-44
Origem
Nacional
Coleções
-
Artigos de Periódicos (40021)Engenharias (2426)
Este item está licenciado na Creative Commons License