Synthesis of nanocrystalline nickel oxide powders via glycine-nitrate combustion

Abstract

NiO is a candidate material for a variety of potential applications, for example, active optical filters, antiferromagnetic layers, coloring agents for enamel, pigments, catalysts, cathode materials for alkaline batteries and temperature sensors. Nanocrystalline nickel oxide powders have been synthesized by combustion technique using glycine as a fuel aand nitrate as an oxidizer. the precursor solution was heated to evaporate water, yelding a viscous liquid. it ignite and underwent self-sustaining combustion, producing an ash composed of the oxide product. The as-synthesized particles have been characterized by X-ray diffraction (XRD), and acanning electron microscopy (SEM). Nanocrystalline nickel oxide was possible to be obtained from fuel-lean ratios. The smallest crystallite size was obtained under fuel-lean (1.09) formulation. The size of the NiO nanoparticles varied from 4 to 18 nm.

O NiO é um material candidato para uma variedade de aplicações: filtros óticos ativos, camadas antiferromagnéticas, agentes corantes para vidrados, pigmenos, catalisadores, cátodos como materiais para baterias alcalinas e sensores de temperatura. Pós de óxido de níquel nanocristalino foram sintetizados pela técnica de combustão, usando glicina como combustível e nitrato como oxidante. A solução precursora foi aquecida até evaporar a água, gerando um líquido viscoso. Ela sofre ignição e combustão autosustentada, produzindo uma cinza a qual é composta de um óxido como produto. As partículas como-sintetizadas foram caracterizadas pela difração de raios X (DRX), e microscopia eletrônica de varredura (MEV). O óxido de níquel nanocristalino foi obtido de reações deficientes em combustível. O menor tamanho de cristalino foi obtido com a formulação deficiente em combustível (0.09). Os tamanhos de nanopartículas de NiO variaram de 4 a 18nm.