Preparação e caracterização de catalisadores para a polimerização de olefinas
Fecha
2003Autor
Nivel académico
Grado
Tipo
Resumo
Neste trabalho foram preparados catalisadores metalocênicos suportado em aduto de MgCl2 (MgCl2.nEtOH) com morfologia controlada. Foi utilizado TiCl4 como agente de desalcoolação e CpTiCl3 como precursor metalocênico. Os catalisadores foram testados em polimerização de etileno. O catalisador mais ativo foi o preparado com o suporte desalcoolado com razão TiCl4/EtOH = 1, decrescendo para a razão igual a 1,3. O polímero com maior peso molecular foi o obtido com o catalisador preparado com o mesmo ...
Neste trabalho foram preparados catalisadores metalocênicos suportado em aduto de MgCl2 (MgCl2.nEtOH) com morfologia controlada. Foi utilizado TiCl4 como agente de desalcoolação e CpTiCl3 como precursor metalocênico. Os catalisadores foram testados em polimerização de etileno. O catalisador mais ativo foi o preparado com o suporte desalcoolado com razão TiCl4/EtOH = 1, decrescendo para a razão igual a 1,3. O polímero com maior peso molecular foi o obtido com o catalisador preparado com o mesmo suporte, sendo que a sua a polidispersão diminui com o aumento da razão TiCl4/EtOH. Para os catalisadores preparados em hexano a sua atividade diminui com o aumento do temperatura de preparação do catalisador, enquanto o peso molecular do polímero aumentou. Comportamento inverso foi verificado para os preparados em tolueno. A polidispersão do polímero não variou significativamente. ...
Abstract
Metallocene supported catalysts were prepared using MgCl2.nEtOH adducts as the support. TiCl4 was employed in order to remove the alcohol from the support and CpTiCl3 was used as the metallocene compound. The catalysts were tested in ethylene polymerization. The most active catalyst was that one prepared with the support dealcoholated with molar ratio TiCl4/ETOH = 1. The polymer with higher molecular weight was that one obtained with this catalyst. Was observed a decrease on the catalyst activi ...
Metallocene supported catalysts were prepared using MgCl2.nEtOH adducts as the support. TiCl4 was employed in order to remove the alcohol from the support and CpTiCl3 was used as the metallocene compound. The catalysts were tested in ethylene polymerization. The most active catalyst was that one prepared with the support dealcoholated with molar ratio TiCl4/ETOH = 1. The polymer with higher molecular weight was that one obtained with this catalyst. Was observed a decrease on the catalyst activity and a increase on the polymer molecular weight with the increase of the temperature catalyst preparation when the solvent was n- hexane. For the catalyst preparation in toluene these results were the opposite. ...
Institución
Universidade Federal do Rio Grande do Sul. Escola de Engenharia. Curso de Engenharia de Materiais.
Colecciones
-
Tesinas de Curso de Grado (37015)Tesinas Ingenierías (5789)
Este ítem está licenciado en la Creative Commons License