dc.description.abstractNos curtumes, as operações de ribeira geram quantidades elevadas de resíduos sólidos. Durante o tratamento das peles na ribeira, especificamente na etapa de pré-descarne é removido material adiposo que constitui a camada subcutânea da pele, esse resíduo é composto de gorduras e proteínas. Através dos processos de digestão/extração e winterização, é possível produzir oleína dos resíduos sólidos do pré-descarne. A oleína é um composto de triacilgliceróis formado por ácidos graxos insaturados com potencial para ser convertido a polióis e utilizado na manufatura de poliuretanos (PU), gerando uma alternativa para substituir os derivados de petróleo comumente utilizados nesse processo. Este trabalho tem como objetivo produzir polióis de oleína por glicerólise alcalina e, a partir dos polióis produzidos, preparar espumas flexíveis de poliuretano (EFPUs) Empregou-se um planejamento experimental fatorial completo 24 com 4 repetições no ponto central para otimizar a produção de polióis de oleína. As espumas EFPUs foram preparadas com razões molares NCO/OH de 1,1 e 1,2, usando-se poliisocianatos alifáticos lineares e cíclicos, água como agente de expansão e surfactante de silicone. O poliol à base de oleína (PO2 - produzido na melhor condição de glicerólise alcalina estudada) apresentou índice de hidroxila elevado (acima de 300 mg KOH.g-1) e funcionalidade próxima a 3. A estabilidade térmica da espuma de poliuretano produzida foi maior que a estabilidade térmica do poliol de oleína. A densidade, o alongamento na ruptura e a resiliência das espumas de PU foram dependentes da razão molar de NCO/OH. As microscopias de MEV das espumas de PU mostraram estruturas das células como polígono totalmente fechados, outros com aberturas e muitas paredes enrugadas. Os materiais extrativos das espumas de PU foram inferiores a 3%, indicando a formação de estrutura reticulada.pt_BR
dc.description.abstractIn the tanneries, the beamhouse generate high amounts of solid waste. During the treatment of skins in beamhouse, specifically in pre-fleshing stage is removed adipose material that constitutes the subcutaneous layer of the skin, this residue is composed of fats and proteins. Through the processes of digestion/extraction and winterization, it is possible to produce olein from the solid waste from the pre-fleshing. Olein is a triacylglycerol compound formed by unsaturated fatty acids that can be converted to polyols and used to manufacture polyurethane, an alternative to replace the petroleum derivatives, commonly employed in the process. This work aims to obtain polyol from olein through alkaline glycerolysis and, from the polyols produced, to produce flexible polyurethane foams (FPUFs). A 24 full factorial design with 4 repetitions at the central point was used to optimize the production of olein polyols. EFPUs were prepared with NCO/OH molar ratios of 1.1 and 1.2, linear and cyclic aliphatic polyisocyanates, water as blowing agent and silicone surfactant. The olein-based polyol (PO2 - produced in the best alkaline glycerolysis condition studied) showed high hydroxyl number (above 300 mg KOH.g-1) and functionality near to 3. Thermal stability of produced polyurethane foams was greater than thermal stability of olein polyol. Density, elongation at break and resilience of PU foams have been dependents of NCO/OH ratio. SEM microscopy of FPUFs show cells structures with polygon totally closed, others with openings and many wrinkled walls. Extractable materials of polyurethane foams was lower than 3% indicating that a crosslinked structure is formed.en
dc.format.mimetypeapplication/pdfpt_BR
dc.language.isoporpt_BR
dc.rightsOpen Accessen
dc.subjectOleinen
dc.subjectÁcidos graxospt_BR
dc.subjectAlkaline glycerolysisen
dc.subjectPolióispt_BR
dc.subjectOlein polyolsen
dc.subjectGlicerólisept_BR
dc.subjectFlexible polyurethane foamsen
dc.subjectEspuma de poliuretanopt_BR
dc.titleModificação de oleína para obtenção de espumas de poliuretanopt_BR
dc.typeDissertaçãopt_BR
dc.contributor.advisor-coPetzhold, Cesar Liberatopt_BR
dc.identifier.nrb001061877pt_BR
dc.degree.grantorUniversidade Federal do Rio Grande do Sulpt_BR
dc.degree.departmentEscola de Engenhariapt_BR
dc.degree.programPrograma de Pós-Graduação em Engenharia Químicapt_BR
dc.degree.localPorto Alegre, BR-RSpt_BR
dc.degree.date2017pt_BR
dc.degree.levelmestradopt_BR


Thumbnail
   

Este item está licenciado na Creative Commons License

Mostrar registro simples