dc.contributor.advisorStrohaecker, Telmo Robertopt_BR
dc.contributor.authorIsrael, Charles Leonardopt_BR
dc.date.accessioned2009-08-15T04:17:12Zpt_BR
dc.date.issued2005pt_BR
dc.identifier.urihttp://hdl.handle.net/10183/16863pt_BR
dc.description.abstractEste trabalho tem por objetivo a avaliação comparativa da resistência ao desgaste abrasivo e a resistência ao impacto Charpy de um ferro fundido nodular austemperado (temperaturas de austêmpera em 260 e 300 ºC), de um ferro fundido nodular temperado em óleo e revenido a 200 ºC, e de um ferro fundido branco com alto teor de Cr, temperado ao ar e revenido a 400 ºC. Para a caracterização dos ferros fundidos, foi utilizada microscopia óptica e ensaios mecânicos de tração e dureza. Na avaliação dos corpos-de-prova que sofreram teste de desgaste, foram avaliadas a perda de massa, rugosidade superficial, dureza Vickers e microscopia eletrônica de varredura na superfície desgastada. Para a avaliação da resistência ao impacto foi utilizado o ensaio Charpy e as superfícies de fratura foram observadas em microscópio eletrônico de varredura. Para os ensaios de desgaste, observou-se que até 120h de ensaio, o ferro fundido branco alto cromo apresentava menor perda de massa, se comparado com os demais materiais. A partir de 144h houve uma inversão de desempenho com o ferro fundido nodular austemperado a 300 ºC, apresentando menor taxa de desgaste até o final do ensaio em 196h. Nos resultados de impacto o material que apresentou maior tenacidade foi o Ferro fundido nodular austemperado a 300 ºC. No ensaio de desgaste acredita-se que foi a presença de austenita retida na microestrutura do austemperado a 300 ºC (superior aos demais) o fator decisivo. Para a resistência ao impacto, alem da quantidade de austenita retida, a baixa dureza do austemperado a 300 ºC e a baixa quantidade de grafita provocaram a maior resistência deste tipo fundido.pt_BR
dc.description.abstractThis work aims to evaluate the abrasive wear resistance and the charpy resistance of three different materials. The first one was an austempered ductile iron (austempering temperatures of 260 and 300 ºC), the second was a quenched and tempered ductile cast iron and the third was a white cast iron high chromium (quenched and tempered - 400 ºC). Optical microscopy, traction and hardness tests were employed in the mechanical characterization of the materials. In the wear test specimens the surface roughness, the Vickers hardness and SEM in the wasted surface were analyzed. In the evaluation of the impact resistance charpy tests were made and the fracture surfaces were analyzed with SEM. It was observed that, in the wear tests, the white cast iron high chromium samples presented the small's mass loss until 120 hours. Up to 144 hours the austempered ductile iron 300ºC samples presented the smaller mass loss. In the impact tests the austempered ductile iron 300ºC was also the material with higher toughness. In the wear tests, the higher level of retained austenite in the 300ºC austempered was the decisive factor. In the impact tests, the low hardness and low graphite amount, ally to the low retained austenite level, were the mainly factors acting in the higher resistance of the 300ºC austempered cast iron.en
dc.format.mimetypeapplication/pdfpt_BR
dc.language.isoporpt_BR
dc.rightsOpen Accessen
dc.subjectFerro fundido nodularpt_BR
dc.subjectMetalografiapt_BR
dc.titleEstudo comparativo da resistência ao desgaste e ao impacto de ferros fundidos de alto desempenhopt_BR
dc.typeDissertaçãopt_BR
dc.identifier.nrb000473435pt_BR
dc.degree.grantorUniversidade Federal do Rio Grande do Sulpt_BR
dc.degree.departmentEscola de Engenhariapt_BR
dc.degree.programPrograma de Pós-Graduação em Engenharia Minas, Metalúrgica e de Materiaispt_BR
dc.degree.localPorto Alegre, BR-RSpt_BR
dc.degree.date2005pt_BR
dc.degree.levelmestradopt_BR