dc.description.abstractCom o objetivo de desenvolver novos revestimentos mais protetores e quantificar a resistência à corrosão resultante, estudou-se a adição de caulinita em novos revestimentos híbridos a base de silanos sobre a liga de alumínio AA7075. Os revestimentos com silanos aqui estudados diferem dos relatados anteriormente na literatura, os quais usualmente contém cargas minerais apenas para a liberação de inibidores de corrosão, enquanto que os revestimentos desenvolvidos no presente estudo contém caulinita lamelar com a finalidade de barreira de difusão para espécies corrosivas. Para tanto, estudou-se primeiramente a esfoliação da caulinita e produção de filmes finos (2-3μm) por diferentes rotas de preparação pelo processo sol-gel, obtendo-se os melhores resultados com o processo envolvendo acidificação final. Os revestimentos e as partículas de caulinita processada foram caracterizados por microscopia ótica, microscopia de varredura eletrônica e difração de raios-X. A resistência à corrosão foi estudada por voltametria cíclica e cronoamperometria, em potencial aplicado entre o potencial de pite e o de repassivação. A maior resitência à corrosão por pites foi obtida para os revestimentos contendo 3% em massa de caulinita, seguido dos com 33% em massa. Estudou-se também preliminarmente a permeação de H2O no revestimento por medidas rápidas de capacitância, após exposição cíclica em soluções contendo cloreto seguidas de secagem, sendo esta metodologia empregada até o momento apenas para tintas bem mais espessas (≈ 300μm). Observou-se que o método é aplicável para medidas no primeiro ciclo de absorção de H2O, concluindo-se que após a primeira exposição, o cloreto continua difundindo, diminuindo o tempo de resistência ao pite.pt
dc.description.abstractAiming to develop more protective new coatings and to quantify the resulting corrosion resistance, new hybrid coatings based on silanes with the addition of kaolinite were produced and applied on the AA7075 aluminum alloy. The studied silane coatings differ from those reported previously in the literature that usually contain mineral fillers to release corrosion inhibitors, since we here developed silane coatings contain lamellar kaolinite as a barrier against the diffusion of corrosive species. For this, we first studied the exfoliation of kaolinite, and production of thin coating (2-3μm) by different preparation routes of the sol-gel process, obtaining the best results with the process of final acidification. Coatings and processed kaolinite particles were characterized by optical microscopy, scanning electron microscopy and X-ray diffraction. The corrosion resistance was evaluated by cyclic voltammetry and chronoamperometry at potentials between that of the repassivation and of the pitting of the substrate alloy. The greatest pitting resistance was obtained for coatings with 3% kaolinite addition, followed by the ones with 33%. The permeation of H2O into the coating was also preliminarily studied by fast capacitance measurements after cyclic exposure to solutions containing chloride followed by drying, a methodology that up to date was only used for much thicker paints (≈ 300μm). It was concluded that in chloride media this method is only applicable for measurements in the first cycle, as after the first exposure, chloride ions continuously permeate into the coating during the drying phase, greatly reducing the time to pit nucleation.en
dc.format.mimetypeapplication/pdfpt_BR
dc.language.isoporpt_BR
dc.rightsOpen Accessen
dc.subjectLigas de alumíniopt_BR
dc.subjectCoatingen
dc.subjectSol-gel processen
dc.subjectResistência à corrosãopt_BR
dc.subjectKaoliniteen
dc.subjectSilanopt_BR
dc.subjectRevestimentopt_BR
dc.subjectLamella chargeen
dc.subjectSol-gelpt_BR
dc.subjectAA7075en
dc.subjectPitting corrosionen
dc.titleEstudo da corrosão de novos revestimentos contendo silanos e caulinita nanolamelar aplicados sobre liga de Al.pt_BR
dc.typeDissertaçãopt_BR
dc.identifier.nrb000953308pt_BR
dc.degree.grantorUniversidade Federal do Rio Grande do Sulpt_BR
dc.degree.departmentEscola de Engenhariapt_BR
dc.degree.programPrograma de Pós-Graduação em Engenharia de Minas, Metalúrgica e de Materiaispt_BR
dc.degree.localPorto Alegre, BR-RSpt_BR
dc.degree.date2014pt_BR
dc.degree.levelmestradopt_BR


Thumbnail
   

Este item está licenciado na Creative Commons License

Mostrar registro simples