dc.description.abstractNo presente trabalho visou-se o estudo de preparação de nanocompósitos PE-argila empregando nova rota de síntese, assim como diferentes fontes de argilas com diferentes complexos. Os nanocompósitos foram sintetizados via polimerização in situ com diferentes percentuais de argila e comparados com o PE puro. As argilas utilizadas foram caracterizadas por difração de raios X (DRX) e capacidade de troca catiônica (CTC). Os materiais poliméricos obtidos foram caracterizados através de diferentes técnicas, entre elas: Espectroscopia Vibracional de Infravermelho (IV), Calorimetria Diferencial de Varredura (DSC), Análise Termo-Gravimétrica (TGA), Microscopia Eletrônica de Transmissão (TEM) e submetidos à Análises Termodinâmico-mecânicas (DMA). As polimerizações foram realizadas em reator Parr, onde avaliou-se a influência do percentual de argila nas propriedades dos nanocompósitos. Os melhores resultados foram obtidos com a utilização do complexo dicloro-1,4-bis-isopropilfenil-acenaftenodiiminaníqueli(II) com a argila Cloisite®15A. As análises de IV mostraram a formação de nanocompósitos PE-argila com cristalinidade maior, melhora as propriedades térmicas observados pelas análises de DSC e melhoras nas propriedades mecânicas dos nanocompósitos de PE quando comparado com o PE puro, a análise de TEM comprovou que houve a esfoliação da argila na matriz polimérica.pt_BR
dc.description.abstractThis work reports the synthesis of PE nanocomposites with clays. The PE nanocomposites were synthesized changing clays source and the catalysts. The polymerization reactions were performed as manner as different incorporation degree of clay in the nanocomposites were achieved and its influence over the PE nanocomposites was evaluated. The properties of these nanocomposites were compared to pure PE. The clays were characterized through X-ray diffraction and cationic exchange capacity. PE nanocomposites were characterized by infrared spectroscopy (IR), differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), transmission electron microscopy (TEM) and thermodynamic- mechanical analysis (DMA). Polymerization reactions were carried out in a Parr reactor. The complex 1,4-bis(2,6-diisopropylphenyl)-acenaphthenediimine- dichloro-nickel(II) activated with methylalumoxane (MAO) showed the bests results. The PE nanocomposites showed improved cristallinity and mechanical properties compared to pure PE. TEM analyses are evidences to PE nanocomposites formation. The enhanced mechanical properties of such nanocompósitos can be justify by the nanometric scale reinforcement due the clay exfoliation in the PE matrix.en
dc.format.mimetypeapplication/pdf
dc.language.isoporpt_BR
dc.rightsOpen Accessen
dc.subjectNanocompósitospt_BR
dc.subjectPolimerizaçãopt_BR
dc.subjectPolímerospt_BR
dc.titleSíntese, caracterização e aplicação de nanocompósitos polímero-argilapt_BR
dc.typeDissertaçãopt_BR
dc.contributor.advisor-coBernardo-Gusmão, Kátiapt_BR
dc.identifier.nrb000673089pt_BR
dc.degree.grantorUniversidade Federal do Rio Grande do Sulpt_BR
dc.degree.departmentInstituto de Químicapt_BR
dc.degree.programPrograma de Pós-Graduação em Ciência dos Materiaispt_BR
dc.degree.localPorto Alegre, BR-RSpt_BR
dc.degree.date2008pt_BR
dc.degree.levelmestradopt_BR


Thumbnail
   

Este item está licenciado na Creative Commons License

Mostrar registro simples