Compositional stability of hafnium aluminates thin films deposited on Si by atomic layer deposition
Fecha
2005Autor
Materia
Abstract
We have used nuclear reaction analyses and Rutherford backscattering spectrometry to investigate quantitatively the compositional stability of hafnium aluminate thin films deposited on Sis001d by atomic layer deposition using HfCl4/H2O and AlsCH3d3/H2O precursors. It was found that increasing Al/Hf deposition cycles ratio leads to increasing oxygen deficiency in the as-deposited films as well as to increasing metal losses sup to ,15%d from the films after rapid thermal annealing at 1000 °C. Fur ...
We have used nuclear reaction analyses and Rutherford backscattering spectrometry to investigate quantitatively the compositional stability of hafnium aluminate thin films deposited on Sis001d by atomic layer deposition using HfCl4/H2O and AlsCH3d3/H2O precursors. It was found that increasing Al/Hf deposition cycles ratio leads to increasing oxygen deficiency in the as-deposited films as well as to increasing metal losses sup to ,15%d from the films after rapid thermal annealing at 1000 °C. Furthermore, isotopic substitution experiments, showed that incorporation of oxygen from the gas phase is eased in the cases where deposition conditions failed to supply enough oxygen to complete oxides stoichiometry. ...
En
Applied physics letters. Vol. 86, no. 22 (May 2005), 221911, 3 p.
Origen
Estranjero
Colecciones
-
Artículos de Periódicos (39042)Ciencias Exactas y Naturales (5930)
Este ítem está licenciado en la Creative Commons License