Isotopic substitution of N, O, and Si in the thermal oxidation of nitrogen-deposited silicon
Fecha
1999Autor
Materia
Abstract
Nitrogen was deposited on the surface of Si~100! wafers by ion implantation at a very low energy (approximately 20 eV), at fluences between 1 and 1031014 cm22. The samples were thermally oxidized in dry O2 at temperatures between 800 and 1050 °C. Atomic transport of the chemical species involved in the process was investigated by isotopic tracing of N, O, and Si, using depth profiling with nanometric resolution. The obtained results indicate that: (i) the nitrogen atoms deposited on the Si surf ...
Nitrogen was deposited on the surface of Si~100! wafers by ion implantation at a very low energy (approximately 20 eV), at fluences between 1 and 1031014 cm22. The samples were thermally oxidized in dry O2 at temperatures between 800 and 1050 °C. Atomic transport of the chemical species involved in the process was investigated by isotopic tracing of N, O, and Si, using depth profiling with nanometric resolution. The obtained results indicate that: (i) the nitrogen atoms deposited on the Si surface are redistributed during thermal oxidation in O2 within the silicon oxide (oxynitride) film, with maxima at the near-surface and near-interface regions; (ii) during growth, O is fixed not only in the near-interface and near-surface regions like in the thermal growth of SiO2 films on Si, but also in the bulk of the growing oxide (oxynitride) film; and (iii) Si is immobile during the thermal oxidation process. The observed modifications in the mechanisms of thermal growth of SiO2 (SiOxNy) films on Si due to the presence of N are discussed. ...
En
Applied physics letters. New York. Vol. 74, no. 13 (Mar. 1999), p. 1872-1874
Origen
Estranjero
Colecciones
-
Artículos de Periódicos (39552)Ciencias Exactas y Naturales (6036)
Este ítem está licenciado en la Creative Commons License