Nanocompósitos de poliamida 6 com montmorilonitas e xisto
![Thumbnail](/bitstream/handle/10183/13677/000648839.pdf.jpg?sequence=3&isAllowed=y)
Visualizar/abrir
Data
2007Autor
Orientador
Co-orientador
Nível acadêmico
Doutorado
Tipo
Resumo
Neste trabalho foi realizada uma avaliação das propriedades morfológicas, mecânicas e térmicas dos nanocompósitos de poliamida 6 (PA6) utilizando a montmorilonita natural (MMTNa+), as MMT modificadas organicamente (MMT-M2(HT)2N+, MMT-(EtOH)2M1T1N+), o xisto retortado (Xt) e o xisto retortado queimado (Xtq). Os nanocompósitos foram obtidos em câmara de mistura e alguns processamentos foram feitos em extrusora de duplo parafuso. Os nanocompósitos foram caracterizados pelas técnicas de difração de ...
Neste trabalho foi realizada uma avaliação das propriedades morfológicas, mecânicas e térmicas dos nanocompósitos de poliamida 6 (PA6) utilizando a montmorilonita natural (MMTNa+), as MMT modificadas organicamente (MMT-M2(HT)2N+, MMT-(EtOH)2M1T1N+), o xisto retortado (Xt) e o xisto retortado queimado (Xtq). Os nanocompósitos foram obtidos em câmara de mistura e alguns processamentos foram feitos em extrusora de duplo parafuso. Os nanocompósitos foram caracterizados pelas técnicas de difração de raios-X (DRX), de microscopia eletrônica de transmissão (MET), de microscopia de força atômica (MFA), de ensaios mecânicos por tração e de calorimetria diferencial de varredura (DSC). Os nanocompósitos preparados com MMT-(EtOH)2M1T1N+ e Xt apresentaram dispersão homogênea na matriz da poliamida 6, resultando em materiais com melhor desempenho mecânico. Através da DRX, observouse que as argilas promoveram mudança na estrutura cristalina da poliamida, com o favorecimento da formação da fase γ. Com relação ao efeito nucleante das argilas na cristalização da poliamida, a MMT-(EtOH)2M1T1N+ obteve o melhor desempenho como agente de nucleação. As análises de DSC corroboram os resultados de DRX, pois foi observada a inversão de fases de α para γ nos nanocompósitos. A partir, destes resultados foram preparados nanocompósitos, variando o teor de 2 a 15 %g de argila para analisar o efeito da sua concentração nos materiais. Os resultados demonstraram que o aumento do teor de MMTNa+, de MMT-(EtOH)2M1T1N+ e de Xt resultou no decréscimo das propriedades mecânicas e provocou alterações na morfologia e na distribuição das partículas na poliamida. Tanto na DRX quanto no DSC, notou-se que para todos os teores de argila houve o favorecimento da formação da fase cristalina γ na poliamida. Foi realizado um tratamento térmico na poliamida 6 e nos nanocompósitos PA6/MMT-(EtOH)2M1T1N+, PA6/MMTNa+ e PA6/Xt, com a proporção de 95/5 %g. Quando as amostras foram submetidas a temperatura de cristalização baixa, a formação da fase γ é induzida, e à temperatura de cristalização alta predominou a formação do arranjo cristalino α. No intervalo de temperatura de 150 a 180°C, as amostras apresentaram as duas formas cristalinas simultaneamente. A cinética de cristalização não-isotérmica da poliamida 6 e dos nanocompósitos com PA6/MMT-(EtOH)2M1T1N+, PA6/MMTNa+ e PA6/Xt, nas proporções de 98/2%g e de 95/5 %g, foi avaliada pelos modelos cinéticos, como Avrami, Ozawa e combinação de Avrami-Ozawa. Somente o modelo cinético da combinação Avrami-Ozawa representa o processo de cristalização para os nanocompósitos com a MMT-(EtOH)2M1T1N+ e o Xt. Porém este modelo não pode descrever a cinética para o nanocompósito preparado com MMTNa+. Observou-se que para alcançar uma mesma cristalinidade relativa, os nanocompósitos preparados com Xt necessitam de uma velocidade de resfriamento menor do que a poliamida pura. Este comportamento indica que as partículas de argila geram mais sítios de nucleação na matriz polimérica, acelerando a cristalização da poliamida. Os nanocompósitos também foram obtidos com 5 % g de MMTNa+ e de MMT-(EtOH)2M1T1N+ em extrusora de duplo parafuso utilizando poliamidas com pesos moleculares diferentes. Através de DRX e de DSC, observou-se que as poliamidas apresentam diferenças estruturais, pois a PA6 sem processar com peso molecular menor cristaliza em maior proporção na fase γ e a PA6 sem processar com peso molecular maior cristaliza preferencialmente no arranjo α. Os resultados sugerem que o peso molecular da poliamida não afeta as propriedades morfológicas nos nanocompósitos. Observou-se também que os nanocompósitos cristalizam preferencialmente em γ. A adição das argilas não ocasionou aumento na tensão na ruptura quando foi utilizado a poliamida com peso molecular alto, somente aumentando os valores de módulo elástico. ...
Abstract
In this work, an assessment of the morphological, mechanical, and thermal properties of polyamide 6 nanocomposites (PA 6) was carried out using natural montmorillonite (MMTNa+), organically modified MMT (MMT-M2(HT)2N+, MMT-(EtOH)2M1T1N+), pyrolyzed oil shale (Xt), and burned pyrolyzed oil shale (Xtq). The nanocomposites were obtained in a mixing chamber, and some other processing were carried out in a twin screw extruder. Nanocomposites were characterized by means of X-ray diffraction (DRX), tr ...
In this work, an assessment of the morphological, mechanical, and thermal properties of polyamide 6 nanocomposites (PA 6) was carried out using natural montmorillonite (MMTNa+), organically modified MMT (MMT-M2(HT)2N+, MMT-(EtOH)2M1T1N+), pyrolyzed oil shale (Xt), and burned pyrolyzed oil shale (Xtq). The nanocomposites were obtained in a mixing chamber, and some other processing were carried out in a twin screw extruder. Nanocomposites were characterized by means of X-ray diffraction (DRX), transmission electronic microscopy (TEM), atomic force microscopy (AFM), mechanical tests and differential scanning calorimetry (DSC). The nanocomposites prepared with MMT-(EtOH)2M1T1N+ and Xt showed homogeneous dispersion in the matrix of polyamide 6, generating materials with a better mechanical performance. With the DRX, it was observed that clays produced change in the crystalline structure of the polyamide, favoring the development of the γ phase. As for the nucleating effect of clays on polyamide crystallization, MMT-(EtOH)2M1T1N+ had the best performance as a nucleating agent. DSC analyses confirmed the DRX results, since an inversion of phases from α to γ was observed in the nanocomposites. These results served as a basis for the preparation of nanocomposites with clay content varying from 2 to 15 %wt to analyze the effect of clay concentration on materials. Results showed that an increase in the content of MMTNa+, of MMT-(EtOH)2M1T1N+, and of Xt caused a decrease in mechanical properties and caused alterations in the morphology and in the distribution of the particles into polyamide. In both DRX and DSC it was noticed that, for every amount of clay content, the formation of the γ crystalline phase in the polyamide was favored. A thermal treatment in polyamide 6 and in the PA6/MMT-(EtOH)2M1T1N+, PA6/MMTNa+, and PA6/Xt nanocomposites was carried out in the proportion of 95/5 %wt. When the samples were subjected to a low crystallization temperature, the formation of the γ phase was induced; when they were under high crystallization temperatures, the α crystalline arrangement prevailed. In the temperature interval between 150 and 180ºC, the samples presented the two different crystalline forms simultaneously. Non-isothermal crystallization kinetics of polyamide 6 and of nanocomposites containing PA6/MMT-(EtOH)2M1T1N+, PA6/MMTNa+, and PA6/Xt, in proportions of 98/2 %wt and of 95/5 %wt, was evaluated through the use of kinetic models, such as Avrami, Ozawa, and the combination Avrami-Ozawa. Only the combined Avrami-Ozawa kinetic model could represent the crystallization process of nanocomposites containing MMT-(EtOH)2M1T1N+ and Xt. However, this model cannot describe the kinetics of nanocomposites prepared with MMTNa+. It was verified that, in order for the same relative crystallinity to be obtained, nanocomposites prepared with Xt need lower cooling speed than pure polyamide. This behavior indicates that clay particles create more nucleation sites in the polymeric matrix, accelerating polyamide crystallization. Nanocomposites were also obtained with 5 %wt MMTNa+ and MMT-(EtOH)2M1T1N+ in a twin screw extruder using polyamides of different molecular weight values. Through DRX and DSC, it was observed that these polyamides have differences in structure, because unprocessed PA6 of lower molecular weight crystallizes proportionally more in the γ phase, whereas unprocessed PA6 of higher molecular weight crystallizes preferably in the α arrangement. Results suggest that the polyamide’s molecular weight does not affect nanocomposites’ morphological properties. It was also verified that nanocomposites crystallize preferably in γ. The addition of clays did not affect an increase in tension when a polyamide of high molecular weight was used, only increasing module values. ...
Instituição
Universidade Federal do Rio Grande do Sul. Instituto de Química. Programa de Pós-Graduação em Ciência dos Materiais.
Coleções
-
Ciências Exatas e da Terra (5095)Química (888)
Este item está licenciado na Creative Commons License
![](/themes/Mirage2Novo//images/lume/cc.png)