Confinement effects of ion tracks in ultrathin polymer films
Visualizar/abrir
Data
2015Autor
Tipo
Abstract
We show direct experimental evidence that radiation effects produced by single MeV heavy ions on a polymer surface are weakened when the length of the ion track in the material is confined into layers of a few tens of nanometers. Deviation from the bulk (thick film) behavior of ion-induced craters starts at a critical thickness as large as ∼40 nm, due to suppression of long-range additive effects of excited atoms along the track. Good agreement was found between the experimental results, molecu ...
We show direct experimental evidence that radiation effects produced by single MeV heavy ions on a polymer surface are weakened when the length of the ion track in the material is confined into layers of a few tens of nanometers. Deviation from the bulk (thick film) behavior of ion-induced craters starts at a critical thickness as large as ∼40 nm, due to suppression of long-range additive effects of excited atoms along the track. Good agreement was found between the experimental results, molecular dynamic simulations, and an analytical model. ...
Contido em
Physical review letters. Melville. Vol. 114, no. 11 (Mar. 2015), 118302, 5 p.
Origem
Estrangeiro
Coleções
-
Artigos de Periódicos (39774)Ciências Exatas e da Terra (6068)
Este item está licenciado na Creative Commons License