New isopropylmaltol - Ti synthesis and its use as a catalyst for olefin polymerization
Fecha
2014Autor
Materia
Resumo
Este artigo mostra a síntese e caracterização do ligante isopropilmaltol obtido a partir do furfural e também um novo complexo diclorobis-(3-hidroxi-2-isopropil-4-pirona)titânio(IV) com estrutura cis. Dados de ressonância magnética nuclear de 1H, análise elementar e UV-Vis confirmam a formação do complexo. Este complexo foi estudado em reações de polimerização de etileno utilizando metilaluminoxano (MAO) como co-catalisador. A atividade catalítica deste complexo é baixa, entretanto foram obtido ...
Este artigo mostra a síntese e caracterização do ligante isopropilmaltol obtido a partir do furfural e também um novo complexo diclorobis-(3-hidroxi-2-isopropil-4-pirona)titânio(IV) com estrutura cis. Dados de ressonância magnética nuclear de 1H, análise elementar e UV-Vis confirmam a formação do complexo. Este complexo foi estudado em reações de polimerização de etileno utilizando metilaluminoxano (MAO) como co-catalisador. A atividade catalítica deste complexo é baixa, entretanto foram obtidos polietilenos com alto peso molecular que são interessantes para diferentes aplicações. ...
Abstract
This report describes a new synthesis of isopropylmaltol from furfural. This organic compound was used as ligand to obtain a new complex, the dichlorobis-(3-hydroxy-2-isopropyl-4-pyrone) titanium(IV). 1H nuclear magnetic ressonance, elemental analysis and UV-Vis analysis confirm the complex formation. This complex was investigated in ethylene polymerization using methylaluminoxane (MAO) as cocatalyst. The catalytic activity was low, however, there were obtained very high molecular weight polyet ...
This report describes a new synthesis of isopropylmaltol from furfural. This organic compound was used as ligand to obtain a new complex, the dichlorobis-(3-hydroxy-2-isopropyl-4-pyrone) titanium(IV). 1H nuclear magnetic ressonance, elemental analysis and UV-Vis analysis confirm the complex formation. This complex was investigated in ethylene polymerization using methylaluminoxane (MAO) as cocatalyst. The catalytic activity was low, however, there were obtained very high molecular weight polyethylenes, which are interesting for various special applications. ...
En
Journal of the Brazilian Chemical Society. São Paulo. Vol. 25, no. 12 (Dec. 2014), p. 2258-2265